| About |
|---|
| A steel-filled, liquid epoxy designed for maintaining and/or repairing tooling, mold-making, and leveling equipment. Intended Use: Holding fixtures for intricate parts; filling and leveling equipment; repairing hard-to-reach areas where a flowable epoxy is needed; duplicating or tracing masters; short run dies and molds Product features: Low viscosity, self-leveling liquid Castable Low shrinkage Machinable to metallic finish&& |
| Product Description | |
|---|---|
| Supplier | Devcon |
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Low Viscosity,Low contractility,Machinable |
| Availabilitys | North America |
| Process Methods | casting |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 2.10 | g/cm³ | |
| Specific volume | 0.473 | cm³/g | |
| Shrinkage rate | |||
| MD | 0.060 | % | ASTM D2566 |
| Solid content | |||
| by Volume | 100 | % | |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 1.2 | kV/mm | ASTM D149 |
| Dielectric constant | 67.5 | ASTM D150 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Heat resistant temperature | |||
| Dry | 121 | ℃ | |
| Wet | 49 | ℃ | |
| Tensile shear strength | 19.3 | MPa | ASTM D1002 |
| Uncured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| Curing time | 16 | hr |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 85 | ASTM D2240 | |
| Tensile modulus | 5860 | MPa | ASTM D638 |
| bending strength | 51.6 | MPa | ASTM D790 |
| compressive strength | 70.3 | MPa | ASTM D695 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Linear coefficient of thermal expansion | |||
| MD | 6.8E-5 | 1/℃ | ASTM D696 |
| Thermal conductivity coefficient | 0.58 | W/m/K | ASTM C177 |
| Thermosetting components | |||
| Component A | 按容量计算的混合比: 3.0 按重量计算的混合比: 9.0 | ||
| Component B | 按容量计算的混合比: 1.0 按重量计算的混合比: 1.0 | ||
| storage stability | |||
| 24 ℃ | 45 | min | |
| Thermosetting mixed viscosity | 15000 to 25000 | cP |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |