| About |
|---|
| Alumina ceramic bead-filled epoxy system with outstanding abrasion resistance for severe service conditions with particulate greater than 1/8″ Intended Use: Repair scrubbers, ash handling systems, pipe elbows, screens, and chutes; recontour chippers, bins, hoppers, bunkers, separators, diester tables; protect exhausters, chutes, launderers, housing fans, crushers, and breakers Product Features: Outstanding resistance to a wide range of chemicals Services temperatures to 300°F Non-sagging&& |
| Product Description | |
|---|---|
| Supplier | Devcon |
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Good wear resistance,Solvent resistance |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 2.20 | g/cm³ | |
| Specific volume | 0.466 | cm³/g | |
| Shrinkage rate | |||
| MD | 0.060 | % | ASTM D2566 |
| Solid content | |||
| by Volume | 100 | % | |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | 41.0 | ASTM D150 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Heat resistant temperature | |||
| Dry | 149 | ℃ | |
| Wet | 60 | ℃ | |
| Tensile shear strength | 10.2 | MPa | ASTM D1002 |
| Uncured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| Curing time | 16 | hr |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 87 | ASTM D2240 | |
| tensile strength | 29.0 | MPa | |
| bending strength | 49.2 | MPa | ASTM D790 |
| compressive strength | 75.8 | MPa | ASTM D695 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Linear coefficient of thermal expansion | |||
| MD | 5.2E-5 | 1/℃ | ASTM D696 |
| Thermosetting components | |||
| Component A | 按容量计算的混合比: 2.0 按重量计算的混合比: 2.0 | ||
| Component B | 按容量计算的混合比: 1.0 按重量计算的混合比: 1.0 | ||
| storage stability | |||
| 24 ℃ | 30 | min |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |