DeWAL DW 220 - SOLIAO

About
A Skived PTFE film that is produced from a modified homopolymer PTFE resin containing <1% of a fully fluorinated comonomer. The incorporation of the comonomer yields a material with improved electrical and physical properties. This film can be thermally fused to itself. The modified homopolymer resin exhibits chemical resistance equivalent to that of a standard homopolymer PTFE. It's tensile strength is approximately 10% higher and the elongation is approximately 30% higher than for a standard homopolymer PTFE. With its ability to be heat fused, this film finds applications in the convoluted PTFE hose industry as a inner liner material.&&

About

A Skived PTFE film that is produced from a modified homopolymer PTFE resin containing <1% of a fully fluorinated comonomer. The incorporation of the comonomer yields a material with improved electrical and physical properties. This film can be thermally fused to itself. The modified homopolymer resin exhibits chemical resistance equivalent to that of a standard homopolymer PTFE. It's tensile strength is approximately 10% higher and the elongation is approximately 30% higher than for a standard homopolymer PTFE. With its ability to be heat fused, this film finds applications in the convoluted PTFE hose industry as a inner liner material.&&

Product Description
Generic	PTFE
Material Status	Commercial: Active
Features	Good Electrical Properties,Good Tensile Strength,Solvent resistance,Homopolymer
Availabilitys	North America,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Thickness	25.4 to 1020	nm

film	Nominal value	Unit	Test method
tensile strength
MD, yield	24.8	MPa	ASTM D882
Tensile strain
MD, fracture	250	%	ASTM D882

THERMAL	Nominal value	Unit	Test method
Continuous use temperature	260	℃

Electrical performance	Nominal value	Unit	Test method
Dielectric strength	98	kV/mm	ASTM D149

Supplementary information	Nominal value	Unit
Core ID	7.62	cm
Maximum Roll OD	356	mm
Width	6.35 to 1140	mm

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.