| About |
|---|
| Diakon® CMG334V is a Polymethyl Methacrylate Acrylic material. It is available in Europe for injection molding. Primary attribute of Diakon® CMG334V: Flame Rated. Typical application of Diakon® CMG334V: Automotive&& |
| Product Description | |
|---|---|
| Supplier | Lucite |
| Generic | PMMA |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 2.2 | g/10min | ISO 1133 |
| Shrinkage rate | 0.40 to 0.70 | % | |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.30 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.0 | kJ/m² | ISO 179-1eA |
| Charpy Unnotch Impact strength | 20 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | 2.0 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 105 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 102 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| — | 117 | ℃ | ISO 306/A |
| — | 109 | ℃ | ISO 306/B |
| Linear coefficient of thermal expansion | |||
| MD | 7.1E-5 | 1/℃ | ASTM E831 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 | |
| Igniting temperature of the hot wire | 650 | ℃ | IEC 60695-2-13 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.490 | ISO 489 | |
| Transmittance | |||
| 2000 µm | 92.0 | % | ASTM D1003 |
| Haze | |||
| 2000 µm | 0.40 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 98 | ISO 2039-2 | |
| Ball hardness | |||
| H 961/30 | 185 | MPa | ISO 2039-1 |
| tensile strength | 83.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 5.0 | % | ISO 527-2 |
| Bending modulus | 3200 | MPa | ISO 178 |
| bending strength | 115 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Hopper temperature | 50 to 100 | °C | |
| Barrel rear temperature | 200 to 250 | °C | |
| Barrel middle temperature | 220 to 290 | °C | |
| Barrel front temperature | 220 to 300 | °C | |
| Nozzle temperature | 220 to 280 | °C | |
| Mold temperature | 50 to 90 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |