| Diamaloy ABSPC 754M- Medical Grade resin is a non-reinforced, flame retardant, antimony-, bromine-, and chlorine free. Diamaloy ABSPC 754M is naturally opaque and is available in custom colors. High heat and impact resistance.&& |
| Product Description | |
|---|---|
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,Halogen free,High Heat Resistance,Amorphous,V-0 |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.17 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 265℃，5.0kg | 30 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.40 to 0.80 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| injection molding | 2410 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 52.1 | MPa | ASTM D638 |
| yield | 55.8 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 140 | % | ASTM D638 |
| yield | 5.1 | % | ASTM D638 |
| Bending modulus | 2280 | MPa | ASTM D790A |
| bending strength | |||
| Yield, injection molding | 82.7 | MPa | ASTM D790A |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 750 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 96.1 | ℃ | ASTM D648 |
| Vicat Softening Temp | 122 | ℃ | ASTM D1525 9 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – hot air dryer | 93 | °C | |
| Drying time – hot air dryer | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 221 to 232 | °C | |
| Barrel middle temperature | 227 to 235 | °C | |
| Barrel front temperature | 249 to 260 | °C | |
| Nozzle temperature | 249 to 263 | °C | |
| Mold temperature | 66 to 79 | °C | |
| Notes |
|---|
| 1. Cytotoxicity test. |
| 2. V0 all Colors 0.0591 |
| 3. Typical properties: these are not to be construed as specifications. |
| 4. Procedure A |
| 5. Type I |
| 6. Type I, 2.0 in/min |
| 7. Method I (3 point load), 0.050 in/min |
| 8. Method I (3 point load) |
| 9. Rate B (120°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |