| About |
|---|
| Diamond ABS 3001MC is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in North America. Characteristics include: Flame Rated REACH Compliant RoHS Compliant WEEE Compliant&& |
| Product Description | |
|---|---|
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Electroplating,HB |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.04 | g/cm³ | ISO 1183 |
| — | 1.05 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 30 | g/10min | ISO 1133 |
| Shrinkage rate | 0.40 to 0.60 | % | ISO 294-4 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 22 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | 220 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 91.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 78.0 | ℃ | ISO 75-2/B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| All colors | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 108 | ASTM D785 | |
| R-level | 108 | ISO 2039-2 | |
| tensile strength | |||
| yield | 47.0 | MPa | ASTM D638 |
| yield | 43.0 | MPa | ISO 527-2 |
| Bending modulus | |||
| — | 2480 | MPa | ASTM D790 |
| — | 2310 | MPa | ISO 178 |
| bending strength | |||
| — | 78.4 | MPa | ASTM D790 |
| — | 70.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80.0 to 90.0 | °C | |
| Drying time | 2.0 to 5.0 | hr | |
| Barrel rear temperature | 190 to 260 | °C | |
| Barrel middle temperature | 190 to 260 | °C | |
| Barrel front temperature | 190 to 260 | °C | |
| Mold temperature | 40.0 to 80.0 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Procedure A |
| 3. 2.0 in/min |
| 4. 0.050 in/min |
| 5. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |