| About |
|---|
| Diamond ABS 9501-1001S is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by extrusion, sheet extrusion, or thermoforming and is available in North America. Applications of Diamond ABS 9501-1001S include marine applications and sheet. Characteristics include: Flame Rated REACH Compliant RoHS Compliant WEEE Compliant Impact Resistant&& |
| Product Description | |
|---|---|
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance |
| Availabilitys | North America |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 230℃，10.0kg | 7.3 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -40℃ | 150 | J/m | |
| 0℃ | 320 | J/m | |
| 23℃ | 520 | J/m | |
| Dart impact equipped with measuring instruments | |||
| -40℃ | 17.0 | J | |
| -30℃ | 30.0 | J | |
| 0℃ | 42.0 | J | |
| 23℃ | 45.0 | J |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 91.0 | ℃ | |
| 0.45 MPa, annealed | 100 | ℃ | |
| 1.8 MPa, unannealed, 3.2 mm | 76.0 | ℃ | |
| 1.8 MPa, annealed, 3.18 mm | 95.0 | ℃ | |
| Vicat Softening Temp | |||
| — | 105 | ℃ | ASTM D1525 4 |
| — | 95.0 | ℃ | ASTM D1525 5 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 101 | ASTM D785 | |
| Tensile modulus | |||
| 0℃ | 2510 | MPa | |
| 23℃ | 2100 | MPa | |
| tensile strength | |||
| Yield, 0 ℃ | 47.0 | MPa | |
| Yield, 23 ℃ | 43.0 | MPa | |
| Yield, 71 ℃ | 29.0 | MPa | |
| Fracture, 0 ℃ | 41.0 | MPa | |
| Fracture, 23 ℃ | 34.0 | MPa | |
| Fracture, 71 ℃ | 20.0 | MPa | |
| Tensile strain | |||
| Fracture, 0 ℃ | 21 | % | |
| Fracture, 23 ℃ | 20 | % | |
| Fracture, 71 ℃ | 15 | % | |
| Bending modulus | |||
| 2% secant, -40 ℃ | 2570 | MPa | |
| 2% secant, 23 ℃ | 2300 | MPa | |
| 2% secant, 71 ℃ | 1810 | MPa | |
| bending strength | |||
| -40℃ | 106 | MPa | |
| 23℃ | 69.0 | MPa | |
| 71℃ | 42.0 | MPa |
| Process Conditions | |||
|---|---|---|---|
| Squeeze description | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80 to 85 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.10 | % | |
| Barrel 1 zone temperature | 177 to 185 | °C | |
| Barrel 2 zone temperature | 191 to 196 | °C | |
| Barrel 3 zone temperature | 199 to 210 | °C | |
| Barrel 4 zone temperature | 213 to 218 | °C | |
| Barrel 5 zone temperature | 218 to 232 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 1.7 in/min |
| 3. Rate A (50°C/h), Loading 1 (10 N) |
| 4. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |