Diamond Plastics Laser HDPE HX 17

About
Laser HDPE HX 17 is a rigid, very good free flowing Laser Sinter powder. Suitable for parts from above 1,5mm. 100% reusable. No blending and mixing of old and new powder. It can be varnished with comon plastic paint. Consistent against acid and base, water, alcohol, oil and gasoline. It can be welded and crosslinked. Very smooth surface, epecially suitable for masterforms for vacuum casting. Medium particle size:50µm. Max.particle size: 80µm. Recomended layerheight: 100µm&&

About

Laser HDPE HX 17 is a rigid, very good free flowing Laser Sinter powder. Suitable for parts from above 1,5mm. 100% reusable. No blending and mixing of old and new powder. It can be varnished with comon plastic paint. Consistent against acid and base, water, alcohol, oil and gasoline. It can be welded and crosslinked. Very smooth surface, epecially suitable for masterforms for vacuum casting. Medium particle size:50µm. Max.particle size: 80µm. Recomended layerheight: 100µm&&

Product Description
Generic	热塑性聚酯
Material Status	Commercial: Active
Features	Good Rigidity,Alkali resistant,Good surface appearance,Crosslinked,Renewable resources,Ethanol tolerance,Good liquidity,Acidproof,Good wear resistance,Grease resistance,Welding,Gasoline resistance
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	3D Printing, Laser Sintering/Melting

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.970	g/cm³	ISO 1183/A
Apparent density	0.50	g/cm³	DIN 53466
Melt Flow Rate	20	g/10min	ISO 1133
Average particle size	50	µm

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	2000	MPa	ISO 527-2
tensile strength	21.0	MPa	ISO 527-2
Tensile strain
fracture	5.5	%	ISO 527-2

IMPACT	Nominal value	Unit	Test method
Notched impact strength of cantilever beam
23℃	10	kJ/m²	ISO 180

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	75.0	℃	ISO 306
Melting temperature	130	℃	DIN 53736

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.