| About |
|---|
| Outline: CZ-1030 is a pitch based carbon fiber reinforced PPS compound that has excellent self lubricant performance with low wear, and low friction properties. Color: Black&& |
| Product Description | |
|---|---|
| Supplier | DIC Corporation |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Low coefficient of friction,Self-lubricating,Good wear resistance,V-0 |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.43 | g/cm³ | ASTM D792 |
| Shrinkage rate | ASTM D955 | ||
| MD | 0.25 | % | ASTM D955 |
| TD | 1.1 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.080 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 45 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | 220 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 265 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | ASTM D696 | ||
| MD：-30~90℃ | 2.0E-5 | 1/℃ | ASTM D696 |
| TD：-30~90℃ | 2.0E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+7 to 1.0E+8 | ohms·cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | ||
| M-level | 100 | ASTM D785 | |
| R-level | 120 | ASTM D785 | |
| Tensile modulus | 10000 | MPa | ASTM D638 |
| tensile strength | 115 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 0.80 | % | ASTM D638 |
| Bending modulus | 9000 | MPa | ASTM D790 |
| bending strength | 170 | MPa | ASTM D790 |
| compressive strength | 130 | MPa | ASTM D695 |
| Poisson’s ratio | 0.36 | ||
| friction coefficient | ASTM D1894 | ||
| Steel – Dynamic | 0.20 | ASTM D1894 | |
| Steel – Static | 0.20 | ASTM D1894 | |
| Elongation at break and bending | 1.2 | % | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel rear temperature | 300 to 340 | °C | |
| Barrel middle temperature | 300 to 340 | °C | |
| Barrel front temperature | 300 to 340 | °C | |
| Mold temperature | 120 to 150 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. P=150KPa, V=0.3m/s |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |