| About |
|---|
| Outline: FZ-2100 is an un-filled polyphenylene sulfide compound with excellent ductility and flexibility. Color: Black and Natural&& |
| Product Description | |
|---|---|
| Supplier | DIC Corporation |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Good flexibility,Ductility |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.35 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 1.30 | % | ASTM D995 |
| TD | 1.50 | % | ASTM D995 |
| Water absorption rate | |||
| 23℃，24hr | 0.02 | % | ASTM D570 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 200 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 110 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 4.0E-5 | 1/℃ | ASTM D696 |
| TD | 4.0E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+16 | Ω.cm | ASTM D257 |
| Insulation strength | |||
| 1.60 mm | 23 | KV/mm | ASTM D149 |
| Dielectric constant | |||
| 23℃ | 3.3 | 1 MHz | ASTM D150 |
| Dissipation factor | |||
| 23℃ | 2.0E-3 | 1 MHz | ASTM D150 |
| Arc resistance | 125 | sec | ASTM D495 |
| Compared to the leakage tracing index | 135 | V | ASTM D3638 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75mm | V-0 | UL 94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 40 | J/m | ASTM D256 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 100 | M 级 | ASTM D785 |
| Rockwell hardness | 121 | R 级 | ASTM D785 |
| tensile strength | |||
| 23℃ | 80 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | > 15 | % | ASTM D638 |
| Poisson’s ratio | 0.38 | ASTM E132 | |
| Tensile modulus | |||
| 23℃ | 4200 | MPa | ASTM D638 |
| bending strength | |||
| 23℃ | 130 | MPa | ASTM D790 |
| Bending modulus | |||
| 23℃ | 3800 | MPa | ASTM D790 |
| Friction coefficient | |||
| dynamic | 0.40 | ASTM D3702 | |
| static state | 0.35 | ASTM D3702 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion molding conditions | Nominal value | Unit | Test method |
| Injection temperature | |||
| Rear barrel temperature | 300-340 | °C | |
| Central temperature of the barrel | 300-340 | °C | |
| Barrel front temperature | 300-340 | °C | |
| Mold temperature | 120-150 | °C | |
| Drying temperature | 75-75 | °C | |
| Drying time | 3.0 | Hr | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. P=150KPa, V=0.3m/s |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |