| About |
|---|
| DIC.PPS Z-230 Black-2(B)是30%玻纤增强的超韧型PPS复合材料，具有优异的抗冲击性、耐冷热冲击性、耐热水性，和Z-230相比具有低气体放出特性。 |
| Product Description | |
|---|---|
| Supplier | DIC Corporation |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Good flexibility,Low odor |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.56 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| 23℃，24hr | 0.02 | % | ISO 62 |
| Shrinkage rate | |||
| MD | 0.3 | % | ISO 294-4 |
| TD | 0.8 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 12000 | MPa | ISO 527-1 |
| tensile strength | 160 | MPa | ISO 527-1 |
| Tensile strain | |||
| fracture | 2 | % | ISO 527-1 |
| Bending modulus | 11000 | MPa | ISO 178 |
| bending strength | 2.5 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 10 | kJ/m² | ISO 179/1eA | |
| 58 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa | 265 | ℃ | ISO 75-1 |
| Linear coefficient of thermal expansion | |||
| MD：-50~50℃ | 1.5E-5 | /℃ | ISO 11359-2 |
| TD：-50~50℃ | 5.0E-5 | /℃ | ISO 11359-2 |
| Linear coefficient of thermal expansion | |||
| MD：100~200℃ | 1.5 | ×10^-5/℃ | ISO 11359-2 |
| TD：100~200℃ | 13.0 | ×10^-5/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1E+16 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 1 mm | 27 | kV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 1 MHz | 4 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 0.004 | IEC 60250 | |
| Compared to the leakage tracing index | 175 | V | IEC 60112 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Barrel temperature | 290~320 | °C | |
| Mold temperature | 130~150 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |