DILAMID® 6 FVT 30 NAT A是一种聚酰胺6(尼龙6)材料,含有的填充物为30% 玻璃纤维增强材料。 该产品在欧洲有供货,加工方式为:注射成型。&& |
Product Description | |
---|---|
Generic | PA6 |
Material Status | Commercial: Active |
Availabilitys | Europe |
Process Methods | Injection Molding |
Technical Data | |||
---|---|---|---|
PHYSICAL | Nominal value | Unit | Test method |
Density | 1.36 | g/cm³ | ISO 1183 |
Shrinkage rate | |||
MD | 0.30 to 0.35 | % | ASTM D955 |
MECHANICAL | Nominal value | Unit | Test method |
---|---|---|---|
tensile strength | |||
yield | 140 | MPa | ISO 527-2 |
Tensile strain | |||
fracture | 3.0 | % | ISO 527-2 |
Bending modulus | 6.50 | MPa | ISO 178 |
IMPACT | Nominal value | Unit | Test method |
---|---|---|---|
Impact strength of cantilever beam notch | |||
23℃ | 6.5 | kJ/m² | ISO 180 |
THERMAL | Nominal value | Unit | Test method |
---|---|---|---|
Hot deformation temperature | |||
1.8 MPa, unannealed | 200 | ℃ | ISO 75-2/A |
Vicat Softening Temp | |||
B50 | 205 | ℃ | ISO 306 |
Electrical performance | Nominal value | Unit | Test method |
---|---|---|---|
Dielectric strength | 21 | kV/mm | ASTM D149 |
Compared to the leakage tracing index | 500 | V | IEC 60112 |
FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
---|---|---|---|
Igniting temperature of the hot wire | |||
2 mm | 650 | ℃ | IEC 60695-2-13 |
Process Conditions | |||
---|---|---|---|
injection | Nominal value | Unit | Test method |
Drying temperature | 70 to 90 | °C | |
Drying time | 2.0 to 8.0 | hr | |
Recommended maximum moisture content | 0.20 | % | |
Barrel rear temperature | 240 to 280 | °C | |
Barrel middle temperature | 250 to 290 | °C | |
Barrel front temperature | 260 to 300 | °C | |
Nozzle temperature | 255 to 295 | °C | |
Processing (melt) temperature | 260 to 300 | °C | |
Mold temperature | 70 to 110 | °C |
Notes |
---|
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |