| (DOMAMID A1-021-V15-H2-DB) Polyamide 6, 15% glass fiber reinforced, heat stabilized, for injection moulding, black&& |
| Product Description | |
|---|---|
| Supplier | DOMO |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Heat Stabilized |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.23 | g/cm³ | |
| Melt Volume Rate | |||
| 275℃，5 kg | 75.0 | cm³/10min | |
| Shrinkage rate | |||
| TD：23℃，72 hrs | 1.1 to 1.3 | % | |
| MD：23℃，72 hrs | 0.50 to 0.70 | % | |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 2.7 | % | |
| Viscosity number | |||
| 96% H2SO4 | 145 | cm³/g | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 5600 | MPa | |
| tensile strength | |||
| fracture | 120 | MPa | |
| Tensile strain | |||
| fracture | 3.0 | % | |
| Bending modulus | 4800 | MPa | |
| bending strength | 180 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 5.5 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| 23℃ | 35 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 215 | ℃ | |
| 1.8 MPa, unannealed | 190 | ℃ | |
| Vicat Softening Temp | 210 | ℃ | |
| Melting temperature | 221 | ℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | < 100 | mm/min |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 75 to 85 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 250 to 290 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 50% RH |
| 3. 0.20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |