| (DOMAMID 6G30STC1) Polyamide 6, 30% glass fiber reinforced, improved impact resistance also at low temperature, for injection moulding.&& |
| Product Description | |
|---|---|
| Supplier | DOMO |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | low-temperature impact resistance |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.32 | g/cm³ | |
| Melt Volume Rate | |||
| 275℃，5 kg | 25.0 | cm³/10min | |
| Shrinkage rate | |||
| TD：23℃，72 hrs | 0.90 to 1.1 | % | |
| MD：23℃，72 hrs | 0.40 to 0.60 | % | |
| Viscosity number | |||
| 96% H2SO4 | 145 | cm³/g | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 8600 | MPa | |
| tensile strength | |||
| fracture | 130 | MPa | |
| Tensile strain | |||
| fracture | 4.5 | % | |
| Bending modulus | 7700 | MPa | |
| bending strength | 225 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 21 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| 23℃ | 100 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 20 | kJ/m² | |
| Notched impact strength of cantilever beam | |||
| 23℃ | 90 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 210 | ℃ | |
| 1.8 MPa, unannealed | 195 | ℃ | |
| Vicat Softening Temp | 205 | ℃ | |
| Melting temperature | 221 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+13 | ohms | |
| Volume resistivity | 1.0E+15 | ohms·cm |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | HB | ||
| Burning rate | < 100 | mm/min |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 75 to 85 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 240 to 270 | °C | |
| Mold temperature | 90 to 120 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 50% RH |
| 3. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |