| About |
|---|
| (DOMAMID 6AF) Polyamide 6, improved flowability, for injection moulding&& |
| Product Description | |
|---|---|
| Supplier | DOMO |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 275℃，5 kg | 225 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD：23℃，72 hrs | 1.0 to 1.2 | % | |
| MD：23℃，72 hrs | 0.90 to 1.1 | % | |
| Viscosity number | |||
| 96% H2SO4 | 125 | cm³/g | ISO 307 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 无断裂 | ISO 179/1eU | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 4.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 无断裂 | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 180 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 70.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 205 | ℃ | ISO 306 |
| Melting temperature | 221 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Compared to the leakage tracing index | |||
| Solution A | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | < 100 | mm/min | FMVSS 302 |
| Flame retardant level | |||
| 0.75 mm | V-2 | ||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-2 | ||
| Glowing wire flammability index | |||
| 1.0-3.0 mm | 850 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 1-3 mm | 725 | ℃ | IEC 60695-2-13 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Shortname | PA6,M,12-030 | ISO 1874 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 120 | ISO 2039-2 | |
| Tensile modulus | 3100 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 80.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 50 | % | ISO 527-2/50 |
| Bending modulus | 2700 | MPa | ISO 178 |
| bending strength | 100 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 75 to 85 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 230 to 250 | °C | |
| Mold temperature | 60 to 90 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 50% RH |
| 3. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |