| About |
|---|
| Polyamide 6, medium viscosity, 30% glass fiber reinforced, natural&& |
| Product Description | |
|---|---|
| Supplier | DOMO |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 275℃，5 kg | 40.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD：23℃，72 hrs | 0.95 | % | ISO 294-4 |
| MD：23℃，72 hrs | 0.35 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 1.7 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.20 | % | ISO 62 |
| Viscosity (H2SO4 (sulfuric acid)) | 145 | cm³/g | ISO 307 |
| Ash Content | |||
| 650℃ | 30 | % | ISO 3451 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 11 | kJ/m² | ISO 179/1eA |
| 23℃ | 14 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 75 | kJ/m² | ISO 179/1eU |
| 23℃ | 95 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 210 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 220 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 217 | ℃ | ISO 306/A50 |
| B50 | 214 | ℃ | ISO 306 |
| Melting temperature | 221 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+14 | ohms | VDE 0303-3 |
| Volume resistivity | 1.0E+15 | ohms·cm | VDE 0303-3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | |||
| 2.0 mm | 40 | mm/min | ISO 3795 |
| Flame retardant level | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 | |
| Igniting temperature of the hot wire | |||
| 2 mm | 650 | ℃ | VDE 0471/2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 9300 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| fracture | 180 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 3.6 | % | ISO 527-2/1A/5 |
| Bending modulus | 7200 | MPa | ISO 178 |
| bending strength | 270 | MPa | ISO 178 |
| Ball hardness | 217 | MPa | ISO 2039-1 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |