| About |
|---|
| SEC 39001 Specialty Ethylene Copolymer is an ethylene butene copolymer, offers excellent processing and performance in various applications such as footwear and wire & cable. Main Characteristics: Pellet form Excellent processability Applications: Foam application Halogen free flame retardance (HFFR) compound&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Negative |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.890 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 4.5 | g/10min | ASTM D1238 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | 64.0 | kN/m | ASTM D624 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -41.0 | ℃ | Internal Method |
| Vicat Softening Temp | 58.0 | ℃ | ASTM D1525 |
| Melting temperature | |||
| DSC | 80.0 | ℃ | Internal Method |
| Crystallization peak temperature | 65 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shaw A, molded | 87 | ASTM D2240 | |
| Shaw’s D, molded | 36 | ASTM D2240 | |
| Tensile modulus | |||
| 100% secant | 4.24 | MPa | ASTM D638 |
| tensile strength | |||
| limit | 13.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 600 | % | ASTM D638 |
| Bending modulus | ASTM D790 | ||
| 1% cut, molded | 33.0 | MPa | ASTM D790 |
| 2% cut, molded | 34.0 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 508 mm/min |
| 3. Compression Molded. 508 mm/min |
| 4. Die C |
| 5. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |