Dow Corning® QP1-30

About
Translucent, Uncatalyzed Silicone Rubber Base APPLICATIONS Dow Corning® QP1 Silicone Elastomer Bases are an uncatalyzed material designed for compounding into elastomer used for part fabrication of medical devices and device components including those intended for implantation in humans for less than 30 days and non-implant applications. DESCRIPTION Dow Corning QP1 Silicone Elastomers are a one-part high consistency rubber base which is supplied absent any catalyst. Once compounded with peroxide it can be used to fabricate parts by extrusion, calendaring or molding. When compounded and cured as indicated, the resulting elastomer consists of cross-linked dimethyl and methyl-vinyl siloxane copolymers and reinforcing silica.&&

About

Translucent, Uncatalyzed Silicone Rubber Base APPLICATIONS Dow Corning® QP1 Silicone Elastomer Bases are an uncatalyzed material designed for compounding into elastomer used for part fabrication of medical devices and device components including those intended for implantation in humans for less than 30 days and non-implant applications. DESCRIPTION Dow Corning QP1 Silicone Elastomers are a one-part high consistency rubber base which is supplied absent any catalyst. Once compounded with peroxide it can be used to fabricate parts by extrusion, calendaring or molding. When compounded and cured as indicated, the resulting elastomer consists of cross-linked dimethyl and methyl-vinyl siloxane copolymers and reinforcing silica.&&

Product Description
Supplier	Dow Corning
Generic	硅酮
Material Status	Commercial: Active
Features	Good coloring
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.09	g/cm³	ASTM D792

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s A	28		ASTM D2240

elastic body	Nominal value	Unit	Test method
tensile strength	10.8	MPa	ASTM D412
200% strain	0.800	MPa	ASTM D412
Tensile strain
fracture	860	%	ASTM D412
tear strength	13.5	kN/m	ASTM D624
Compression deformation
177℃，22 hr	39	%	ASTM D395

Notes
1. Typical properties: these are not to be construed as specifications.
2. Die B
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.