DOWLEX™ 2045.01 G

About
DOWLEX 2045.01G Polyethylene Resin is designed for the production of a wide variety of industrial and consumer films. Films made from this resin exhibit a combination of excellent toughness and tear resistance. The product also delivers very good processability on conventional LLDPE machinery. DOWLEX 2045.01G Polyethylene Resin contains slip and antiblock additives. Applications: Thin gauge industrial & consumer films Heavy duty films Complies with: EU, No 10/2011 U.S. FDA 21 CFR 177.1520(c)3.2a Consult the regulations for complete details.&&

About

DOWLEX 2045.01G Polyethylene Resin is designed for the production of a wide variety of industrial and consumer films. Films made from this resin exhibit a combination of excellent toughness and tear resistance. The product also delivers very good processability on conventional LLDPE machinery. DOWLEX 2045.01G Polyethylene Resin contains slip and antiblock additives. Applications: Thin gauge industrial & consumer films Heavy duty films Complies with: EU, No 10/2011 U.S. FDA 21 CFR 177.1520(c)3.2a Consult the regulations for complete details.&&

Product Description
Supplier	DOW
Generic	Linear low density polyethylene
Material Status	Commercial: Active
Availabilitys	Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.922	g/cm³	ASTM D792
Melt Flow Rate
190℃，2.16kg	1.0	g/10min	ASTM D1238

film	Nominal value	Unit	Test method
film thickness
test	51	µm
Membrane puncture resistance
51 µm	19.0	J/cm³	Internal Method
Membrane strength			ASTM D882
MD：51 µm	346	J/cm³	ASTM D882
TD：51 µm	351	J/cm³	ASTM D882
Secant modulus			ASTM D882
2% secant, MD: 51 µ m	194	MPa	ASTM D882
2% secant, TD: 51 µ m	233	MPa	ASTM D882
tensile strength			ASTM D882
MD, yield, 51 µ m	11.0	MPa	ASTM D882
TD, yield, 51 µ m	12.0	MPa	ASTM D882
MD, fracture, 51 µ m	55.0	MPa	ASTM D882
TD, fracture, 51 µ m	50.0	MPa	ASTM D882
Tensile strain			ASTM D882
MD, fracture, 51 µ m	830	%	ASTM D882
TD, fracture, 51 µ m	890	%	ASTM D882
Drop hammer impact
51 µm	290	g	ASTM D1709-A
Elmandorf tear strength			ASTM D1922
MD：51 µm	900	g	ASTM D1922
TD：51 µm	1200	g	ASTM D1922

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	108	℃	ASTM D1525
Melting temperature	122	℃	DSC

optical performance	Nominal value	Unit	Test method
gloss
45°，51 µm	54		ASTM D2457
Haze
51 µm	13	%	ASTM D1003

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	190 to 240	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.