DOWLEX™ 2610G Polyethylene Resin is specifically designed for large/high output cast film lines to make high performance industrial stretch films. Films made from DOWLEX™ 2610G Polyethylene Resin exhibit an excellent balance of processability, mechanical and stretchability performance properties. DOWLEX™ 2610G Polyethylene Resin is to be used as a core resin in coextruded cast film structures for films in the thickness range between 17 and 35 microns. Applications: Cast Stretch Wrap Film Complies with: EU, No 10/2011 U.S. FDA FCN 1539 Consult the regulations for complete details.

About

DOWLEX™ 2610G Polyethylene Resin is specifically designed for large/high output cast film lines to make high performance industrial stretch films. Films made from DOWLEX™ 2610G Polyethylene Resin exhibit an excellent balance of processability, mechanical and stretchability performance properties. DOWLEX™ 2610G Polyethylene Resin is to be used as a core resin in coextruded cast film structures for films in the thickness range between 17 and 35 microns. Applications: Cast Stretch Wrap Film Complies with: EU, No 10/2011 U.S. FDA FCN 1539 Consult the regulations for complete details.

Product Description
Supplier	DOW
Generic	Linear low density polyethylene
Material Status	Commercial: Active
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.924	g/cm³	ASTM D792
Melt Flow Rate
190℃，2.16kg	4.0	g/10min	ISO 1133

film	Nominal value	Unit	Test method
film thickness	23	µm
Membrane puncture force (23 µ m)	31.0	N	ASTM D5748
Tensile strength
MD: yield, 23 µ m, extruded film	6.00	MPa
TD: yield, 23 µ m, extruded film	6.50	MPa
MD: fracture, 23 µ m, extruded film	30.0	MPa
TD: fracture, 23 µ m, extruded film	22.0	MPa
Tensile strain
MD, fracture, 23 µ m, extruded film	440	%
TD, fracture, 23 µ m, extruded film	630	%
Drop hammer impact
23 µ m, cast thin film	> 100	g	ISO 7765-1/A
Elmandorf tear strength
MD: 23 µ m, cast thin film	150	g
TD: 23 µ m, cast thin film	440	g
Film Puncture Elongation（23.0 µm）	120	mm
Film tensile performance – maximum tensile force	37000	g
Film tensile performance – maximum elongation	400	%	Internal Method

Process Conditions
Squeezing instructions	Nominal value	Unit	Test method
extrusion	Nominal value	Unit	Test method
Melt Temperature	220 to 280	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.