| About |
|---|
| DOWLEX™ 2629UE Polyethylene Resin for rotational and injection moulding is specifically designed for applications requiring excellent environmental stress crack resistance and impact strength combined with low warpage and good processing. Processing and Stabilisation: DOWLEX™ 2629UE Polyethylene Resin is fully heat and UV stabilised resulting in a wide processing latitude, good colour retention and long life expectancy. The powder version is named DOWLEX™ 2629.10UE Polyethylene Resin. Applications: Intermediate bulk containers Drums for chemicals Boats Freezer containers Fish crates Small tanks Complies with: EU, No 10/2011 U.S. FDA 21 CFR 177.1520(c)3.1a Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.935 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 4.0 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | ASTM D1693 | ||
| 50 ℃, 10% emulsifier, molded | 400 | hr | ASTM D1693 |
| 50 ℃, 100% emulsifier, molded | > 1000 | hr | ASTM D1693 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Multi axial instrumented impact energy | ISO 6603-2 | ||
| -20 ℃, roll forming | 66.0 to 88.0 | J | ISO 6603-2 |
| 23 ℃, roll forming | 54.0 to 72.0 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 65.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 119 | ℃ | ASTM D1525 3 |
| Melting temperature | 124 | ℃ | DSC |
| Crystallization peak temperature | |||
| DSC | 110 | ℃ | DSC |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 57 | ISO 868 | |
| tensile strength | |||
| Yield, molding | 17.5 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, molded | 650 | % | ISO 527-2 |
| Bending modulus | |||
| Compression Molding | 645 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Plates of 3-4 mm thickness. |
| 3. Rate B (120°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |