DOWLEX™ NG 5056G

About
DOWLEX™ NG 5056G Polyethylene Resin is a next generation linear low density polyethylene resin designed for high quality blown film applications requiring a combination of excellent optical properties, tear strength and sealability, and a very good toughness/stiffness balance. DOWLEX NG 5056G Polyethylene Resin is also designed to offer a very low gel level making it ideal for use in lamination films and other specialty packaging. Note: DOWLEX NG 5056G Polyethylene Resin should comply with FDA regulation 177.1520 and with most European food contact regulations when used unmodified and processed according to good manufacturing practices for food contact applications. Please, contact your nearest Dow office regarding food contact compliance statements. The purchaser remains responsible for determining whether the use complies with all relevant regulations. Applications: High clarity tissue overwrap Produce bags Food packaging films Lamination film&&

About

DOWLEX™ NG 5056G Polyethylene Resin is a next generation linear low density polyethylene resin designed for high quality blown film applications requiring a combination of excellent optical properties, tear strength and sealability, and a very good toughness/stiffness balance. DOWLEX NG 5056G Polyethylene Resin is also designed to offer a very low gel level making it ideal for use in lamination films and other specialty packaging. Note: DOWLEX NG 5056G Polyethylene Resin should comply with FDA regulation 177.1520 and with most European food contact regulations when used unmodified and processed according to good manufacturing practices for food contact applications. Please, contact your nearest Dow office regarding food contact compliance statements. The purchaser remains responsible for determining whether the use complies with all relevant regulations. Applications: High clarity tissue overwrap Produce bags Food packaging films Lamination film&&

Product Description
Supplier	DOW
Generic	Linear low density polyethylene
Material Status	Commercial: Active
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.919	g/cm³	ASTM D792
Melt Flow Rate
190℃，2.16kg	1.1	g/10min	ISO 1133

film	Nominal value	Unit	Test method
film thickness
test	50	µm
Membrane puncture strength
50 µm	3.50	J	ASTM D5748
Membrane puncture force
50 µm	54.0	N	ASTM D5748
Tensile modulus			ISO 527-3
2% secant, MD, 50 µ m	198	MPa	ISO 527-3
2% secant, TD, 50 µ m	238	MPa	ISO 527-3
tensile strength			ISO 527-3
MD, yield, 50 µ m	7.50	MPa	ISO 527-3
TD, yield, 50 µ m	8.00	MPa	ISO 527-3
MD, fracture, 50 µ m	38.0	MPa	ISO 527-3
TD, fracture, 50 µ m	37.0	MPa	ISO 527-3
Tensile strain			ISO 527-3
MD, fracture, 50 µ m	810	%	ISO 527-3
TD, fracture, 50 µ m	920	%	ISO 527-3
Drop hammer impact
50 µm	450	g	ISO 7765-1/A
Elmandorf tear strength			ASTM D1922
MD：50 µm	890	g	ASTM D1922
TD：50 µm	1100	g	ASTM D1922

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	104	℃	ASTM D1525

optical performance	Nominal value	Unit	Test method
gloss
45°，50 µm	61		ASTM D2457
Haze
50 µm	8.9	%	ISO 14782

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	190 to 240	°C

Notes
1. Typical properties: these are not to be construed as specifications.
2. Compression Molded
3. Blown film extruded at 235°C, 50 microns, 2.5 BUR, 1.55mm die gap.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.