| Dryflex SE is our standard TPE range. It is extremely adaptable and can be used advantageously in many applications. The compounds are easy to process and are optimised for injection moulding. We have developed endless formulations to fulfil different properties and application requirements to optimise the finished component. Grades with improved compression set properties, high temperature resistance or more cost efficient values are an essential part of today’s wide product spectrum. The Dryflex SE unfilled series is favourable when translucency and good scratch resistance are required, as well as when there are high surface finish requirements. The material enables an easy and secure pigmenting. Unfilled grades have excellent flow and mechanical properties. The low density results in lower weight compared to the filled and semi-filled series. Dryflex SE unfilled compounds are available in hardness from 30 to 90 Shore A in natural and black colours but they can easily be coloured.&& |
| Product Description | |
|---|---|
| Generic | TPE |
| Material Status | Commercial: Negative |
| Features | Excellent Processability,Good surface appearance,Renewable resources,Good liquidity,Food contact compliance,High Flexibility,High scratch resistance,Good coloring |
| Availabilitys | Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.890 | g/cm³ | ISO 2781 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 15 seconds | 90 | ISO 868 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ISO 37 | ||
| TD, 100% strain | 4.90 | MPa | ISO 37 |
| TD, 300% strain | 6.00 | MPa | ISO 37 |
| tensile strength | |||
| TD, fracture | 15.2 | MPa | ISO 37 |
| Tensile strain | |||
| TD, fracture | 750 | % | ISO 37 |
| tear strength | 51 | kN/m | ISO 34-1 |
| Compression deformation | ISO 815 | ||
| 23℃，72 hr | 41 | % | ISO 815 |
| 70℃，22 hr | 61 | % | ISO 815 |
| 100℃，22 hr | 76 | % | ISO 815 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Barrel rear temperature | 170 to 190 | °C | |
| Barrel middle temperature | 180 to 200 | °C | |
| Barrel front temperature | 190 to 210 | °C | |
| Nozzle temperature | 200 to 220 | °C | |
| Mold temperature | 15 to 50 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method C, Crescent |
| 3. Type B |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |