| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA 410 |
| Material Status | Commercial: Active |
| Features | Renewable resources,Heat Stabilized |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.52 | g/cm³ | ISO 1183 |
| Water absorption rate | 1.10 | % | ISO 62 |
| Shrinkage rate | |||
| normal | 0.80 | % | ISO 294-4 |
| parallel | 0.40 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ultimate tensile strength | 170 | MPa | ISO 527-1/-2 |
| Tensile strain | |||
| fracture | |||
| Tensile modulus | |||
| desiccation | 3.0 | % | ISO 527-1/-2 |
| Conditional | 12000 | MPa | ISO 527-1-2 |
| Conditional | 3.5 | % | ISO 527-1/-2 |
| desiccation | 16000 | MPa | ISO 527-1-2 |
| bending strength | |||
| Conditional | 250 | MPa | ISO 178 |
| desiccation | 335 | MPa | ISO 178 |
| Bending modulus | MPa | ||
| Conditional | 11.3 | GPa | ISO 178 |
| desiccation | 14.6 | GPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Linear coefficient of thermal expansion | |||
| TD | 50.0 | µm/m-℃ | ISO 11359-1/-2 |
| MD | 42.0 | µm/m-℃ | ISO 11359-1/-2 |
| Melting temperature | |||
| 10℃ / min | 250 | ℃ | ISO 11357-1/-3 |
| Hot deformation temperature | |||
| 0.45 MPa | 245 | ℃ | ISO 75-1/2 |
| 载荷下热变形温度(1.8 MPa) | |||
| ## | 215 | ℃ | ISO 75-1/-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 80 | kJ/m² | ISO 179/1eU |
| -30℃ | 80 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| -30℃ | 12 | kJ/m² | ISO 179/1eA |
| 23℃ | 15 | kJ/m² | ISO 179/1eA |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |