| Ducor 1100L is a homopolymer with a conventional molecular weight distribution and is formulated with a general-purpose additive package. Ducor 1100L is designed for injection moulding applications, closures and houseware. Food Contact Applications: This grade is in compliance with most regulations regarding food contact applications (EU, FDA). Specific information is available upon request.&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Food contact compliance,Homopolymer |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.910 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 6.0 | g/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 1.5 | kJ/m² | ISO 179/1eA |
| 23℃ | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 16 | kJ/m² | ISO 179/1eU |
| 23℃ | 140 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 1.3 | kJ/m² | ISO 180-1A |
| 23℃ | 3.5 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 55.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 85.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| — | 154 | ℃ | ISO 306/A |
| — | 90.0 | ℃ | ISO 306/B |
| Melting temperature | |||
| DSC | 163 | ℃ | ISO 3146 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 1000 µ m, injection molding | 60 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 34.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | > 50 | % | ISO 527-2/50 |
| yield | 9.0 | % | ISO 527-2/50 |
| Tensile creep modulus | |||
| 1000 hr | 380 | MPa | ISO 899-1 |
| shear modulus | 750 | MPa | ISO 6721-2 |
| Ball hardness | |||
| H358/30 | 74.0 | MPa | ISO 2039-1 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Elongation <0.5% |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |