| 40% Mineral/Glass Reinforced, Flame Retardant, Polyethylene Terephthalate&& |
| Product Description | |
|---|---|
| Supplier | DuPont |
| Generic | PET |
| Material Status | Commercial: Active |
| Features | Flame Characteristics |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 11000 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 110 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 1.8 | % | ISO 527-2 |
| Bending modulus | 9600 | MPa | ISO 178 |
| bending strength | 170 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.0 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 214 | ℃ | ISO 75-2/A |
| Linear coefficient of thermal expansion | |||
| MD | 2.5E-5 | 1/℃ | |
| TD | 7.8E-5 | 1/℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 1.5 mm | V-1 | IEC 60695-11-10, -20 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.72 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 1.0 | % | |
| MD | 0.20 | % | |
| Ejection temperature | 170 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time – hot air dryer | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Processing (melt) temperature | 270 to 290 | °C | |
| Melt Temperature, Optimum | 280 | °C | |
| Mold temperature | 100 to 130 | °C | |
| Mold Temperature, Optimum | 120 | °C | |
| Hold pressure | 80.0 | MPa | |
| Back Pressure | As low as possible | ||
| Drying Recommended | yes | ||
| Hold Pressure Time | 4.00 | s/mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |