| DURACON® SW-01LV is an Acetal (POM) Copolymer + PE product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated.&& |
| Product Description | |
|---|---|
| Supplier | Polyplastics |
| Generic | Copolymer Polyformaldehyde +PE |
| Material Status | Commercial: Active |
| Features | Low coefficient of friction,HB,Low odor |
| Availabilitys | Europe,Asia Pacific,North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.42 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 7.0 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 190℃，2.16 kg | 6.00 | cm³/10min | ISO 1133 |
| Molding shrinkage | ISO 294-4 | ||
| TD：2.0 mm | 1.7 | % | ISO 294-4 |
| MD：2.0 mm | 2.0 | % | ISO 294-4 |
| Water Absorption | |||
| 23℃，24hr | 0.60 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2 |
| Tensile Strength | 50.0 | MPa | ISO 527-2 |
| Tensile Strain | 20 | % | ISO 527-2 |
| Flexural Modulus | 2500 | MPa | ISO 178 |
| Flexural Strength | 75.0 | MPa | ISO 178 |
| Frictional coefficient | |||
| dynamic | 0.22 | JIS K7218 | |
| Wear factor | JIS K7218 | ||
| 0.060 MPa，0.15 m/sec | 400 | 10^-8 mm³/N·m | JIS K7218 |
| 0.060 MPa，0.15 m/sec | 500 | 10^-8 mm³/N·m | JIS K7218 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 5.4 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Coeff. of linear thermal expansion | |||
| TD：23~55℃ | 1.1E-4 | 1/℃ | Internal Method |
| MD：23~55℃ | 1.1E-4 | 1/℃ | Internal Method |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Color Number | CF2001 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 80 to 90 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Temperature | 190 to 210 | °C | |
| Mold Temperature | 60 to 80 | °C | |
| Injection pressure | 50.0 to 100 | MPa | |
| Screw Speed | 100 to 150 | rpm | |
| Injection Velocity | 5 to 50 | mm/sec | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. vs M90-44, 0.06 MPa, 15 cm/s |
| 3. 0.98 MPa, 30 cm/s |
| 4. Thrust, vs C-Steel, Steel Side |
| 5. Thrust, vs C-Steel, Material Side |
| 6. Thrust, vs M90-44, Material Side |
| 7. Thrust, vs M90-44, M90-44 Side |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |