| About |
|---|
| DuraGrip® 6160BK is designed to be a special purpose Melt Processible Elastomer (MPE) that is easy to use in injection molding and extrusion processes. DGR 6160BK has an excellent soft touch feel and will Bond to Nylon, ABS, PC, PC/ABS. DuraGrip® 6100 series is hygroscopic and requires drying prior to use.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Material Status | Commercial: Active |
| Features | Good bond |
| Availabilitys | North America,Europe,Asia Pacific |
| Process Methods | Extrusion,Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Shore hardness | |||
| Shore A, 5 seconds | 58 | ISO 868 | |
| Shore A, 5 seconds | 58 | ASTM D2240 | |
| Taber abraser | |||
| 1000 cycles, 1.0E+6 g, CS-17 wheel | 189 | mg | ASTM D1044 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile permanent deformation | |||
| 100% strain | 4 | % | ASTM D412 |
| tensile strength | |||
| Yield, 23 ℃ | 6.62 | MPa | ISO 37 |
| Yield, 23 ℃ | 6.62 | MPa | ASTM D412 |
| 100% strain, 23 ℃ | 2.21 | MPa | ISO 37 |
| 100% strain | 2.21 | MPa | ASTM D412 |
| Tensile strain | |||
| Fracture, 23 ℃ | 350 | % | ISO 37 |
| fracture | 350 | % | ASTM D412 |
| tear strength | |||
| 24℃ | 29.4 | kN/m | ASTM D624 |
| Compression deformation | ASTM D395B | ||
| 24℃，22 hr | 21 | % | ASTM D395B |
| 70℃，22 hr | 82 | % | ASTM D395B |
| 100℃，22 hr | 91 | % | ASTM D395B |
| Compression deformation | ISO 815 | ||
| 24℃，22 hr | 21 | % | ISO 815 |
| 70℃，22 hr | 82 | % | ISO 815 |
| 100℃，22 hr | 91 | % | ISO 815 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -65.0 | ℃ | ASTM D746 |
| Embrittlement temperature | -65.0 | ℃ | ISO 812 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air | ASTM D573 | ||
| 70℃，168 hr | 11 | % | ASTM D573 |
| 100% Strain，70℃，168 hr | 2.0 | % | ASTM D573 |
| 100℃，168 hr | 40 | % | ASTM D573 |
| 100% Strain，100℃，168 hr | -5.0 | % | ASTM D573 |
| The rate of change in tensile strength in air | ISO 188 | ||
| 70℃，168 hr | 11 | % | ISO 188 |
| 100% Strain 70℃，168 hr | 2.0 | % | ISO 188 |
| 100℃，168 hr | 40 | % | ISO 188 |
| 100% Strain 100℃，168 hr | -5.0 | % | ISO 188 |
| The rate of change in ultimate elongation in air | ASTM D573 | ||
| 70℃，168 hr | 4.0 | % | ASTM D573 |
| 100℃，168 hr | 18 | % | ASTM D573 |
| Changes in tensile stress during fracture | ISO 1817 | ||
| 70℃，168 hr | 4.0 | % | ISO 1817 |
| 100℃，168 hr | 18 | % | ISO 1817 |
| Volume change | ASTM D471 | ||
| 24℃，168 hr，in Reference Fuel B | 52 | % | ASTM D471 |
| 70℃，168 hr，in ASTM #1 Oil | 12 | % | ASTM D471 |
| 70℃，168 hr，in IRM 903 Oil | 74 | % | ASTM D471 |
| 70℃，168 hr，in Water | 2.0 | % | ASTM D471 |
| Volume change | ISO 1817 | ||
| 24℃，168 hr，in Reference Fuel B | 52 | % | ISO 1817 |
| 70℃，168 hr，in ASTM #1 Oil | 12 | % | ISO 1817 |
| 70℃，168 hr，in IRM 903 Oil | 74 | % | ISO 1817 |
| 70℃，168 hr，in Water | 2.0 | % | ISO 1817 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ASTM D792 |
| Density | 1.07 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：1.59 mm | 1.6 | % | ASTM D955 |
| MD：3.2 mm | 1.5 | % | ASTM D955 |
| TD：1.59 mm | 0.0 | % | ASTM D955 |
| TD：3.2 mm | 0.50 | % | ASTM D955 |
| Shrinkage rate | |||
| TD：1.59 mm | 0.0 | % | ISO 294-4 |
| MD：1.59 mm | 1.6 | % | ISO 294-4 |
| TD：3.2 mm | 0.50 | % | ISO 294-4 |
| MD：3.2 mm | 1.5 | % | ISO 294-4 |
| Apparent viscosity of melt | |||
| 190℃，300 sec^-1 | 354 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 66 | °C | |
| Drying time | 3.0 | hr | |
| Proposed maximum recycled material ratio | 25 | % | |
| Barrel rear temperature | 204 to 221 | °C | |
| Barrel middle temperature | 216 to 227 | °C | |
| Barrel front temperature | 227 to 238 | °C | |
| Nozzle temperature | 227 to 249 | °C | |
| Processing (melt) temperature | 227 to 254 | °C | |
| Mold temperature | 43 to 54 | °C | |
| Injection pressure | 2.76 to 5.52 | MPa | |
| Screw speed | 50 to 150 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |