| About |
|---|
| DURANEX® 2002 is a Polybutylene Terephthalate (PBT) product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include: Flame Rated Good Toughness&& |
| Product Description | |
|---|---|
| Supplier | Polyplastics |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | Good flexibility,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.31 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Flow Rate | 20 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 250℃，2.16 kg | 18.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 1.8 to 2.0 | % | ASTM D955 |
| TD | 1.8 to 2.0 | % | ISO 294-4 |
| MD | 1.8 to 2.0 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.19 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 6.0 | kJ/m² | |
| 23℃ | 6.0 | kJ/m² | |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 190 | kJ/m² | |
| 23℃ | 无断裂 | ||
| Impact strength of cantilever beam notch | |||
| 23℃ | 5.0 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 160 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 150 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 55.0 | ℃ | ASTM D648，ISO 75-2/A |
| Glass transition temperature | 60.0 | ℃ | ISO 11357-2 |
| Vicat Softening Temp | |||
| B50 | 190 | ℃ | ISO 306 |
| Melting temperature | 225 | ℃ | ISO 11357-3, ASTM D3418 |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD | 1.1E-4 | 1/℃ | |
| TD | 1.4E-4 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | |||
| — | 1.0E+16 | ohms·cm | ASTM D257 |
| — | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| — | 17 | kV/mm | ASTM D149 |
| — | 23 | kV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 1 MHz | 3.20 | ASTM D150 | |
| 100 Hz | 4.00 | IEC 60250 | |
| 1 MHz | 3.50 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 1.4E-3 | ||
| 1 MHz | 0.022 | ||
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.71 mm | HB | UL 94 | |
| Extreme oxygen index | 22 | % | ISO 4589-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 78 | ISO 2039-2 | |
| Tensile modulus | |||
| -40℃ | 3100 | MPa | ASTM D638 |
| 23℃ | 3170 | MPa | ASTM D638 |
| 80℃ | 469 | MPa | ASTM D638 |
| 121℃ | 296 | MPa | ASTM D638 |
| — | 2600 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| Yield, -40 ℃ | 101 | MPa | ASTM D638 |
| Yield, 0 ℃ | 75.8 | MPa | ASTM D638 |
| Yield, 23 ℃ | 55.8 | MPa | ASTM D638 |
| Yield, 80 ℃ | 24.8 | MPa | ASTM D638 |
| Yield, 121 ℃ | 17.9 | MPa | ASTM D638 |
| yield | 60.0 | MPa | ISO 527-2/1A/50 |
| fracture | 35.0 | MPa | ISO 527-2/1A/50 |
| 50% strain | 30.0 | MPa | ISO 527-2/1A/50 |
| Tensile strain | |||
| Yield, -40 ℃ | 7.2 | % | ASTM D638 |
| Yield, 0 ℃ | 4.4 | % | ASTM D638 |
| Yield, 23 ℃ | 3.2 | % | ASTM D638 |
| Yield, 80 ℃ | 17 | % | ASTM D638 |
| Yield, 121 ℃ | 23 | % | ASTM D638 |
| yield | 4.0 | % | ISO 527-2/1A/50 |
| Fracture, 23 ℃ | 200 | % | ASTM D638 |
| fracture | 220 | % | ISO 527-2/1A/50 |
| Nominal tensile fracture strain | > 50 | % | ISO 527-2/1A/50 |
| Bending modulus | |||
| 23℃ | 2500 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 80.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 to 130 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Proposed maximum recycled material ratio | 25 | % | |
| Hopper temperature | 20.0 to 50.0 | °C | |
| Barrel rear temperature | 230 to 240 | °C | |
| Barrel middle temperature | 235 to 250 | °C | |
| Barrel front temperature | 235 to 250 | °C | |
| Nozzle temperature | 250 to 260 | °C | |
| Processing (melt) temperature | 235 to 260 | °C | |
| Mold temperature | 65.0 to 93.0 | °C | |
| Injection speed | 中等偏快 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |