| About |
|---|
| Product Description | |
|---|---|
| Supplier | Polyplastics |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | V-0 |
| Availabilitys | North America,Europe,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| 1.54 | g/cm³ | ISO 1183 | |
| 1.54 | g/cm³ | ASTM D792 | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Yield yld | 113 | MPa | ISO 527-1, 2 |
| Yield yld | 112 | MPa | ASTM D638 |
| Tensile Strain | |||
| Break | 2.7 | % | ISO 527-1, 2 |
| Flexural modulus | |||
| 6050 | MPa | ISO 178 | |
| 6080 | MPa | ASTM D790 | |
| Flexural modulus | |||
| 173 | MPa | ISO 178 | |
| 166 | MPa | ASTM D790 | |
| Tensile elongation | 3.5 | % | ASTM D638 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy notched impact strength | |||
| 23℃ | 7.1 | kJ/m² | ISO 179/1eA |
| Izod impact strength (with notch) | |||
| Notch side at the gap | 58 | J/m | ASTM D256 |
| Reverse notch | 440 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, unannealed | 208 | ℃ | ISO 75-2/A |
| 1.82 MPa, unannealed | 208 | ℃ | ASTM D648 |
| Parallel | 4 | ×10-5/℃ | ISO 11359-2 |
| Horizontal Transition | 10 | ×10-5/℃ | ISO 11359-2 |
| 2-7 | ×10-5/℃ | ASTM D696 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 2E16 | ohm·cm | IEC 60093 | |
| 2E16 | ohm·cm | ASTM D257 | |
| Surface resistivity | |||
| 4E16 | ohm | IEC 60093 | |
| 3E16 | ohm | ASTM D257 | |
| Electric strength | |||
| 20 | kV/mm | IEC 60243-1 | |
| 20 | MV/M | ASTM D149 | |
| Compared tracking index | 250 | V | IEC 60112 |
| Arc resistance | 70 | sec | ASTM D495 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | V-0 | UL 94 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |