| About |
|---|
| Duratron® PI D7000 is a Thermoplastic Polyimide product. It is available in Latin America or North America. Primary characteristic: flame rated.&& |
| Product Description | |
|---|---|
| Supplier | Quadrant |
| Generic | TPI |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.37 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| 24hr | 7.0E-3 | % | |
| saturated | 0.038 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 53 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 354 | ℃ | ASTM D648 |
| Glass transition temperature | 349 | ℃ | ASTM D3418 |
| Melting temperature | 304 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD：-40~149℃ | 4.1E-5 | 1/℃ | ASTM E831 |
| Thermal conductivity coefficient | 0.22 | W/m/K | ASTM E1530 |
| Maximum operating temperature | |||
| Air，Continuous | 260 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+13 | ohms | ESD S11.11 |
| Dielectric strength | 16 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1 MHz | 3.20 | ASTM D150 | |
| Dissipation factor | |||
| 1 MHz | < 5.0E-3 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | V-0 | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Pressure limiting speed | |||
| 4：1 safety factor | 0.525 | MPa·m/s | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 90 | ASTM D2240 | |
| Rockwell hardness | |||
| R-level | 128 | ASTM D785 | |
| Tensile modulus | 3720 | MPa | ASTM D638 |
| tensile strength | |||
| — | 121 | MPa | |
| 65℃ | 110 | MPa | |
| 150℃ | 82.7 | MPa | |
| Tensile strain | |||
| fracture | 0.060 | % | ASTM D638 |
| Bending modulus | 3790 | MPa | ASTM D790 |
| bending strength | 172 | MPa | ASTM D790 |
| Compression modulus | 2620 | MPa | ASTM D695 |
| compressive strength | |||
| 10% strain | 186 | MPa | ASTM D695 |
| shear strength | 110 | MPa | ASTM D732 |
| friction coefficient | |||
| Steel – Dynamic | 0.29 | Internal Method | |
| Wear factor | 300 | 10^-8 mm³/N·m | Internal Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method A (Short-Time) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |