| Duratron® T4301 (EXTRUSION) is a Polyamide-imide (PAI) product. It can be processed by extrusion and is available in Latin America or North America. Typical application: Engineering/Industrial Parts. Primary characteristic: flame rated.&& |
| Product Description | |
|---|---|
| Supplier | Quadrant |
| Generic | PAI |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Alkali resistant,Ethanol tolerance,Low coefficient of friction,Acidproof,Good wear resistance,Good compressive strength,Solvent resistance,Heat Stabilized,Hydrocarbons,Insulation,Amorphous,V-0 |
| Availabilitys | North America |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.45 | g/cm³ | ASTM D792 |
| Water absorption rate | ASTM D570 | ||
| 24hr | 0.40 | % | ASTM D570 |
| saturated | 1.5 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 43 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 279 | ℃ | ASTM D648 |
| Maximum operating temperature | |||
| Long Term，Air | 260 | ℃ | |
| Glass transition temperature | 275 | ℃ | ASTM D3418 |
| Linear coefficient of thermal expansion | |||
| MD：-40~149℃ | 2.5E-5 | 1/℃ | ASTM E831 |
| Thermal conductivity coefficient | 0.53 | W/m/K | ASTM F433 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+13 | ohms | Internal Method |
| Dielectric constant | |||
| 1 MHz | 6.00 | ASTM D150 | |
| Dissipation factor | |||
| 1 MHz | 0.037 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | V-0 | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Pressure limiting speed | 0.788 | MPa·m/s | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | ||
| E-level | 70 | ASTM D785 | |
| M-level | 106 | ASTM D785 | |
| Tensile modulus | 6210 | MPa | ASTM D638 |
| tensile strength | |||
| limit | 103 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 3.0 | % | ASTM D638 |
| Bending modulus | 5520 | MPa | ASTM D790 |
| bending strength | |||
| yield | 159 | MPa | ASTM D790 |
| Compression modulus | 6550 | MPa | ASTM D695 |
| compressive strength | |||
| 10% strain | 152 | MPa | ASTM D695 |
| shear strength | 113 | MPa | ASTM D732 |
| friction coefficient | |||
| Steel – Static | 0.20 | Internal Method | |
| Wear factor | 20 | 10^-8 mm³/N·m | ASTM D3702 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. With post-machine cure cycle |
| 3. 1-10, 1=Easier to Machine |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |