| About |
|---|
| Duratron® U1000 is a Polyether Imide (PEI) product. It can be processed by extrusion and is available in Latin America or North America. Applications of Duratron® U1000 include food contact applications and medical/healthcare. Primary characteristic: flame rated.&& |
| Product Description | |
|---|---|
| Supplier | Quadrant |
| Generic | Polyetherimide |
| Material Status | Commercial: Active |
| Features | Acidproof,V-0,Flame Characteristics,Hydrolysis stability,Good Rigidity,High Heat Resistance,Ethanol tolerance,High pressure heat resistance |
| Availabilitys | North America |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.27 | g/cm³ | ISO 1183-1 |
| Water absorption rate | |||
| 23℃，24hr | 16 | mg | ISO 62 |
| 23℃，24hr | 0.19 | % | ISO 62 |
| 23℃，96hr | 34 | mg | ISO 62 |
| 23℃，96hr | 0.40 | % | ISO 62 |
| 23℃，50%RH | 0.70 | % | |
| 23 ℃, saturated | 1.30 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Pendulum impact strength without notch | |||
| 4J | 无断裂 | kJ/m² | ISO 179-1/1eU |
| Pendulum notch impact strength | |||
| 4J | 3.5 | kJ/m² | ISO 179-1/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa | 195 | ℃ | ISO 75-1/-2 |
| Maximum operating temperature | |||
| Short term, in the air | 200 | ℃ | |
| Continuous, in the air, for at least 20000 hours | 170 | °C | |
| Minimum operating temperature | -50 | ℃ | |
| melting point | |||
| DSC,10℃/min | NA | ℃ | ISO 11357-1/-3 |
| Glass transition temperature | |||
| DSC,20℃/min | 215 | ℃ | ISO 11357-1/-2 |
| Thermal conductivity | |||
| 23℃ | 0.24 | W/（K.m） | |
| Linear coefficient of thermal expansion | |||
| 23℃-100℃ | 50 | ×10-6m/(m.K) | |
| 23℃-150℃ | 50 | ×10-6m/(m.K) | |
| Above 150 ℃ | 60 | ×10-6m/(m.K) |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+13 | Ohm/sq. | ANSI/ESD STM 11.11 |
| Dielectric strength | |||
| In oil, 1mm | 27 | kV/mm | IEC60243-1 |
| Volume resistivity | > 1.0E+14 | Ohms.cm | IEC 60093 |
| Relative dielectric constant | |||
| 100 Hz | 3.0 | IEC 60250 | |
| Relative permittivity | |||
| 1 MHz | 3.0 | IEC 60250 | |
| Dielectric loss factor | |||
| 0.002 | IEC 60250 | ||
| Dielectric loss factor angle | |||
| 0.002 | IEC 60250 | ||
| Arc Trajectory Index (CTI) | 175 | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Oxygen index | 47 | % | ISO 4589-1/-2 |
| UL flame retardant rating | |||
| 1.5mm | V-0 | ||
| 3.0mm | V-0 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile stress | |||
| Yield, 50mm/min | 129 | Mpa | ISO 527-1/-2 |
| tensile strength | |||
| 50mm/min | 129 | MPa | ISO 527-1/-2 |
| Tensile strain | |||
| Yield, 50mm/min | 7 | % | ISO 527-1/-2 |
| Fracture, 50mm/min | 13 | % | ISO 527-1/-2 |
| Compressive stress | |||
| 1%,1mm/min | 31 | Mpa | ISO 604 |
| 2%,1mm/min | 61 | Mpa | ISO 604 |
| 5%,1mm/min | 137 | Mpa | ISO 604 |
| Ball hardness | |||
| 10mm | 165 | N/mm² | ISO 2039-1 |
| Rockwell hardness | |||
| 10mm (M level) | 115 | ISO 2039-2 | |
| Tensile modulus of elasticity | |||
| 50mm/min | 3500 | Mpa | ISO 527-1/-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method A (Short-Time) |
| 3. 1-10, 1=Easier to Machine |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |