Durethan® AKV 25 F30 000000

soliao
2024年3月28日
Available in Soliao, PA66

About
Durethan® AKV25F30 000000 (Dry) PA 66, 25 % glass fibers, injection molding, flame retardant&&Durethan® AKV25F30 000000 PA 66, 25 % glass fibers, injection molding, flame retardant&&Durethan® AKV25F30 000000 PA 66, 25 % glass fibers, injection molding, flame retardant&&

Product Description
Supplier	LANXESS
Generic	PA66
Material Status	Commercial: Active
Features	Flame Characteristics,V-0
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.60	g/cm³	ISO 1183
Shrinkage rate			ISO 2577
TD：290℃，2.0 mm	0.70	%	ISO 2577
TD：120℃，2.0 mm，4 hrs	0.30	%	ISO 2577
MD：290℃，2.0 mm	0.40	%	ISO 2577
MD：120℃，2.0 mm，4 hrs	0.10	%	ISO 2577
Water absorption rate
Saturation, 23 ℃	3.9	%	ISO 62
Equilibrium, 23 ℃, 50% RH	1.2	%	ISO 62

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
23℃	10500	MPa	ISO 527-1-2
tensile strength
Fracture, 23 ℃	150	MPa	ISO 527-2/5
Tensile strain
Fracture, 23 ℃	2.2	%	ISO 527-2/5
Bending modulus
23℃	10000	MPa	ISO 178-A
bending strength
23℃	220	MPa	ISO 178-A
Bending strain	2.5	%	ISO 178/A

IMPACT	Nominal value	Unit	Test method
Charpy Unnotch Impact strength			ISO 179/1eU
-30℃	40	kJ/m²	ISO 179/1eU
23℃	50	kJ/m²	ISO 179/1eU
Impact strength of cantilever beam notch
23℃	< 10	kJ/m²	ISO 180-1A
Notched impact strength of cantilever beam			ISO 180/1U
-30℃	40	kJ/m²	ISO 180/1U
23℃	45	kJ/m²	ISO 180/1U

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	238	℃	ISO 75-2/A
0.45 MPa, unannealed	> 240	℃	ISO 75-2/B
Vicat Softening Temp
B120	240	℃	ISO 306/B120
Melting temperature	260	℃	ISO 11357-3
Linear coefficient of thermal expansion
TD：23~55℃	8.0E-5	1/℃	ISO 11359-2
MD：23~55℃	3.0E-5	1/℃	ISO 11359-2

Electrical performance	Nominal value	Unit	Test method
Compared to the leakage tracing index
Solution A	400	V	IEC 60112

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level			UL 94
0.40 mm	V-0		UL 94
0.75 mm	V-0		UL 94
1.00 mm	V-0 5VA		UL 94
3.00 mm	V-0 5VA		UL 94
Glowing wire flammability index			IEC 60695-2-12
0.40 mm	960	℃	IEC 60695-2-12
0.80 mm	960	℃	IEC 60695-2-12
1.5 mm	960	℃	IEC 60695-2-12
3.0 mm	960	℃	IEC 60695-2-12
Igniting temperature of the hot wire			IEC 60695-2-13
0.4 mm	875	℃	IEC 60695-2-13
0.8 mm	775	℃	IEC 60695-2-13
1.5 mm	775	℃	IEC 60695-2-13
3 mm	900	℃	IEC 60695-2-13

Supplementary information	Nominal value	Unit	Test method
ISO Shortname	PA 66,GFHR,14-100,GF25		ISO 1874

Process Conditions
injection	Nominal value	Unit	Test method
Drying Temperature – Dry Air Dryer	80	°C
Drying Time – Dry Air Dryer	2.0 to 6.0	hr
Processing (melt) temperature	270 to 290	°C
Mold temperature	80 to 100	°C
Residual Moisture Content	0.030 to 0.12	%

Notes
1. Typical properties: these are not to be construed as specifications.
2. 60x60x2mm, 4 hr
3. 60x60x2mm, 80°C MT, 600 bar
4. 0.079 in/min
5. 2 mm/min
6. 10°C/min
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.