Durethan® AKV 30

About
注塑成型，30%玻纤增强，最大0.4 mm的UL 94 V-0 灼热丝测试中的温度：在0,75mm处960℃，不含卤素和红磷

Product Description
Supplier	LANXESS
Generic	PA66
Material Status	Commercial: Active
Availabilitys	Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.417	g/cm³	ISO 1183
Shrinkage rate
MD：60x60x2，270℃ / WZ 80℃，600 bar	0.2	%	ISO 2577
Normal, 60x60x2270 ℃/WZ 80 ℃, 600 bar	0.7	%	ISO 2577
Post contraction
Parallel, 60x60x2; 120 ℃; 4 hours	0.1	%	ISO 2577
Normal, 60x60x2; 120 ℃; 4 hours	0.1	%	ISO 2577

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
1 mm/min	10500	MPa	ISO 527-1
Fracture stress
5 mm/min	135	MPa	ISO 527-1
Fracture strain
5 mm/min	2.8	%	ISO 527-1
Bending modulus
2 mm/mim	9300	MPa	ISO 178
bending strength
2 mm/min	215	MPa	ISO 178
Bending strain
2 mm/min	3.1	%	ISO 178
bending strength
3.50% strain, 2 mm/min	120	MPa	ISO 178

THERMAL	Nominal value	Unit	Test method
Melting temperature
10℃ / min	260	℃	ISO 11357-1
Hot deformation temperature
1.8 MPa	224	℃	ISO 75-1/2
0.45 MPa	>250	℃	ISO 75-1/2
Vicat Softening Temp
B120	240	℃	ISO 306
Flame retardant level
1.50 mm	V-0	等级	UL 94
0.40 mm	V-0	等级	UL 94
3.00 mm	V-0	等级	UL 94
Glowing wire flammability index
0.80 mm	960	℃	IEC 60695-2-12
1.5 mm	960	℃	IEC 60695-2-12
3.0 mm	960	℃	IEC 60695-2-12
0.75 mm	750	℃	IEC 60695-2-13
1.5 mm	750	℃	IEC 60695-2-13
3.0 mm	750	℃	IEC 60695-2-13

Electrical performance	Nominal value	Unit	Test method
Compared to the leakage tracing index
Solution A	600		IEC 60112

Other performance	Nominal value	Unit	Test method
Fiberglass content	30	%	ISO 3451-1

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	55	kJ/m²	ISO 180-1A
	10	kJ/m²	ISO 180-1A

Process Conditions
Processing conditions of the sample	Nominal value	Unit	Test method
Processing suggestions	Nominal value	Unit	Test method
Melt temperature	270	°C	ISO 294
Mold temperature	80	°C	ISO 294
Drying temperature	80	°C
Drying time	2-6	h
Remaining moisture content	0.03-0.07	%
Melt temperature	260-270	°C
Mold temperature	80-100	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.