| Durethan® AKV15H2.0 901510 (Dry) PA 66, 15 % glass fibers, injection molding, heat-aging stabilized&&Durethan® AKV15H2.0 901510 PA 66, 15 % glass fibers, injection molding, heat-aging stabilized&&Durethan® AKV15H2.0 901510 PA 66, 15 % glass fibers, injection molding, heat-aging stabilized&& |
| Product Description | |
|---|---|
| Supplier | LANXESS |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Heat Stabilized |
| Availabilitys | Africa & Middle East ,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.23 | g/cm³ | |
| 23℃ | 1.24 | g/cm³ | |
| Apparent density | 0.60 | g/cm³ | |
| Shrinkage rate | |||
| TD：120℃，2.0 mm | 0.20 | % | |
| TD：290℃，2.0 mm | 1.0 | % | |
| MD：120℃，2.0 mm | 0.20 | % | |
| MD：290℃，2.0 mm | 0.70 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 7.0 | % | |
| Equilibrium, 23 ℃, 50% RH | 2.4 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -40℃ | < 10 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 35 | kJ/m² | |
| 23℃ | 35 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| -40℃，3.2mm | — | J/m | |
| 23℃，3.2mm | 64 | J/m | |
| -30℃ | < 10 | kJ/m² | |
| 23℃ | < 10 | kJ/m² | |
| Notched impact strength of cantilever beam | |||
| -30℃ | 30 | kJ/m² | |
| 23℃ | 30 | kJ/m² | |
| Multi axial instrumented impact energy | |||
| -30 ℃, total impact penetration energy | 0.700 | J | |
| 23 ℃, total impact penetration energy | 1.70 | J | |
| Multi axial instrumented peak impact force | |||
| -30℃ | 590 | N | |
| 23℃ | 610 | N |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 4.0 mm | > 249 | ℃ | |
| 0.45 MPa, unannealed | > 250 | ℃ | |
| 1.8 MPa, unannealed, 3.99 mm | 249 | ℃ | |
| 1.8 MPa, unannealed | 230 | ℃ | |
| Vicat Softening Temp | |||
| — | 230 | ℃ | |
| — | > 230 | ℃ | |
| Ball pressure test | |||
| 248℃ | 通过 | ||
| Melting temperature | 263 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD：23~55℃ | 4.0E-5 | 1/℃ | |
| TD：23~55℃ | 9.0E-5 | 1/℃ | |
| 0.75 mm | 125 | ℃ | |
| 15.0 mm | 125 | ℃ | |
| 0.75 mm | 95.0 | ℃ | |
| 1.5 mm | 105 | ℃ | |
| Relative temperature index | |||
| Electrical performance | |||
| Impact mechanical performance | |||
| 0.75 mm | 105 | ℃ | |
| 1.50 mm | 115 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+15 | ohms | |
| Volume resistivity | |||
| 23℃ | 1.0E+15 | ohms·cm | |
| Dielectric strength | |||
| 23 ℃，1 mm | 35 | kV/mm | |
| 23 ℃，3 mm | 35 | kV/mm | |
| Dielectric constant | |||
| 23 ℃，50 Hz | 4.00 | ||
| 23 ℃，1 MHz | 4.00 | ||
| 23 ℃，100 Hz | 4.00 | ||
| Dissipation factor | |||
| 23℃，50 Hz | 0.017 | ||
| 23℃，100 Hz | 9.0E-3 | ||
| 23℃，1 MHz | 9.0E-3 to 0.017 | ||
| Compared to the leakage tracing index | |||
| Solution A | 425 | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| US FMVSS302，> 1.00 mm | passed | ||
| 0.75 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Glowing wire flammability index | |||
| 2.0 mm | 650 | ℃ | |
| Extreme oxygen index | 24 | % |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Shortname | ISO 1874-PA 66, GHR, 14-060, GF15 | ||
| Loss Factor | 0.0200 | ||
| Torsional Loss Modulus | 0.00800 | MPa |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | 190 | MPa | |
| Tensile modulus | |||
| 23℃ | 5900 | MPa | |
| 23℃ | 6200 | MPa | |
| tensile strength | |||
| Fracture, 23 ℃ | 130 | MPa | |
| Fracture, 23 ℃ | 120 | MPa | |
| Tensile strain | |||
| Fracture, 23 ℃ | 9.0 | % | |
| Fracture, 23 ℃ | 3.0 | % | |
| Bending modulus | |||
| 23℃ | 5200 | MPa | |
| bending strength | |||
| 23℃ | 210 | MPa | |
| 23℃ | 200 | MPa | |
| 3.50% strain, 23 ℃ | 175 | MPa | |
| Bending strain | 4.0 | % | |
| Torsional storage modulus | 1.30 | GPa |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying Temperature – Dry Air Dryer | 80 | °C | |
| Drying Time – Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 60x60x2mm, 4 hr |
| 3. 60x60x2mm, 80°C MT, 600 bar |
| 4. 0.039 in/min |
| 5. 0.079 in/min |
| 6. 2 mm/min |
| 7. 10°C/min |
| 8. Tinfoil Electrodes |
| 9. Procedure A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |