Durethan® B 30 S 000000

About

Product Description
Supplier	LANXESS
Generic	PA6
Material Status	Commercial: Active
Availabilitys	Europe,Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Molding shrinkage
Parallel, 150x105x3; 270 ° C/WZ 80 ° C; 500 bar	1.02	%	ISO 2577
Horizontal translation, 150x105x3; 270 ° C/WZ 80 ° C; 500 bar	1.06	%	ISO 2577
Post shrinkage
Parallel, 150x105x3; 120 ° C; 4 hours	0.32	%	ISO 2577
Horizontal translation, 150x105x3; 120 ° C; 4 hours	0.4	%	ISO 2577
Water absorption
Saturation value, 23 ° C	10	%	ISO 62
Equilibrium value, 23 ° C; 50% RH	3	%	ISO 62
Density	1140	kg/m³	ISO 1183
Bulk density	700	kg/m³	ISO 60

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
1 mm/min, dry	3000	MPa	ISO 527-2
1 mm/min, moist cond	1000	MPa	ISO 527-2
Creep, 1h	800	MPa	ISO 899-1
Creep, 1000h	600	MPa	ISO 899-1
Tensile Stress
50 mm/min, dry, yield yld	80	MPa	ISO 527-2
50 mm/min, moist cond, Yield yld	40	MPa	ISO 527-2
Tensile Strain
	20	%	ISO 527-2
50 mm/min, moist cond, Break	>50	%	ISO 527-2
	4	%	ISO 527-2
50 mm/min, moist cond, Yield yld	20	%	ISO 527-2
Flexural Modulus
2 mm/min, dry	2900	MPa	ISO 178
2 mm/min, moist cond	850	MPa	ISO 178

2 mm/min, moist cond	35	MPa	ISO 178
2 mm/min, dry	110	MPa	ISO 178
2 mm/min, 3.5% stress Strain, dry dry	95	MPa	ISO 178
2 mm/min, 3.5% Stress Strain, Wet Cond	25	MPa	ISO 178
Flexural Strain
2 mm/min, dry	6	%	ISO 178/A
2 mm/min, moist cond	8	%	ISO 178/A
Puncture maximum force
23℃	5900	N	ISO 6603-2
-30℃	7300	N	ISO 6603-2
Puncture energy
23℃	90	J	ISO 6603-2
-30℃	85	J	ISO 6603-2
Ball indentation hardness
Dry	140	N/mm²	ISO 2039-1
Wet Cond	50	N/mm²	ISO 2039-1

THERMAL	Nominal value	Unit	Test method
Melting temperature	222	℃	ISO 11357-3
Hot deformation temperature HDT
1.8 MPa	60	℃	ISO 75-1,-2
0.45 MPa	160	℃	ISO 75-1,-2
8.0 MPa	45	℃	ISO 75-1,-2
Vicat softening temperature
50 N; 120 °C/h	200	℃	ISO 306/B
50 N; 50 °C/h	200	℃	ISO 306/B

Parallel	1.0	×10-4/℃	ISO 11359-2
Horizontal transformation	1.1	×10-4/℃	ISO 11359-2

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level
1.5 mm	V-2	calss	UL 94
0.4 mm	V-2	calss	UL 94
Extreme oxygen index	26	%	ISO 4589-2

IMPACT	Nominal value	Unit	Test method
Charpy notched impact strength
23 ℃, dry	<10	kJ/m²	ISO 179/1eA
23 ℃, moist cond	20	kJ/m²	ISO 179/1eA
-30 ℃, dry	<10	kJ/m²	ISO 179/1eA
-30 ℃, moist cond	<10	kJ/m²	ISO 179/1eA

23 ℃, dry	<10	KJ/m²	ISO 180/1A
23 ℃, moist cond	30	KJ/m²	ISO 180/1A

ELECTRICAL	Nominal value	Unit	Test method

100 Hz, dry	4		IEC 60250
100 Hz, moist cond	15		IEC 60250
1 MHz, dry	3.5		IEC 60250
1 MHz, moist cond	4		IEC 60250
Dissipation factor
100 Hz, dry	0.017		IEC 60250
100 Hz, moist cond	0.2		IEC 60250
1 MHz, dry	0.02		IEC 60250
1 MHz, moist cond	0.12		IEC 60250

Dry	1E13	ohm·m	IEC 60093
Wet Cond	1E10	ohm·m	IEC 60093
Surface resistivity
Dry	1E14	ohm	IEC 60093
Wet Cond	1E13	ohm	IEC 60093
Electric strength
	30	kV/mm	IEC 60243-1
	30	kV/mm	IEC 60243-1
Compared tracking index
Method A, CIT	600		IEC 60112
Method B, CIT M	600 M		IEC 60112

Process Conditions
Injection molding	Nominal value	Unit	Test method
Injection molding melt temperature	270	℃
Injection molding mold temperature	80	℃
Drying temperature	80	℃
Drying time	2-6	hr
Residual moisture content	0.03-0.12	%
Melt temperature	260-180	℃
Mold temperature	80-100	℃

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.