| About |
|---|
| Durethan® B30SFN40 000000 (Dry) PA 6, non-reinforced, injection molding, halogen free flame retardant&&Durethan® B30SFN40 000000 PA 6, non-reinforced, injection molding, halogen free flame retardant&&Durethan® B30SFN40 000000 PA 6, non-reinforced, injection molding, halogen free flame retardant&& |
| Product Description | |
|---|---|
| Supplier | LANXESS |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,V-2 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ISO 1183 |
| Apparent density | 0.70 | g/cm³ | ISO 60 |
| Shrinkage rate | |||
| TD：260℃，2.0 mm | 0.90 | % | ISO 294-4 |
| TD：120℃，2.0 mm，2 hrs | 0.30 | % | ISO 294-4 |
| MD：260℃，2.0 mm | 0.90 | % | ISO 294-4 |
| MD：120℃，2.0 mm，2 hrs | 0.30 | % | ISO 294-4 |
| TD：260℃，3.0 mm | 0.90 | % | ISO 2577 |
| TD：120℃，3.0 mm，2 hrs | 0.20 | % | ISO 294-4 |
| MD：260℃，3.0 mm | 0.90 | % | ISO 2577 |
| MD：120℃，3.0 mm，2 hrs | 0.20 | % | ISO 2577 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 10 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 3.0 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | No Break | ISO 179/1eU | |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | < 10 | kJ/m² | ISO 180-1A |
| 23℃ | < 10 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | No Break | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 66.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 166 | ℃ | ISO 75-2/B |
| Melting temperature | 222 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD：23~55℃ | 8.0E-5 | 1/℃ | ISO 11359-2 |
| MD：23~55℃ | 9.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | |||
| Solution A | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | V-2 | UL 94 | |
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 0.80 mm | 960 | ℃ | IEC 60695-2-12 |
| 1.5 mm | 960 | ℃ | IEC 60695-2-12 |
| 3.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 0.8 mm | 875 | ℃ | IEC 60695-2-13 |
| 1.5 mm | 850 | ℃ | IEC 60695-2-13 |
| 3 mm | 750 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 28 | % | ISO 4589-2 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Shortname | PA 6, GFR, 14-030; ISO 1043-PA FR (30) | ISO 1874 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 3400 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 60.0 | MPa | ISO 527-2/5 |
| Yield, 23 ℃ | 90.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Fracture, 23 ℃ | 16 | % | ISO 527-2/5 |
| Yield, 23 ℃ | 4.0 | % | ISO 527-2/50 |
| Nominal tensile fracture strain | |||
| 23℃ | 9.6 | % | ISO 527-2/50 |
| Bending modulus | |||
| 23℃ | 3000 | MPa | ISO 178-A |
| bending strength | |||
| 3.50% strain | 100 | MPa | ISO 178-A |
| 23℃ | 120 | MPa | ISO 178 |
| Bending strain | 5.9 | % | |
| Ball hardness | 135 | MPa | ISO 2039-1 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying Temperature – Dry Air Dryer | 80 | °C | |
| Drying Time – Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (melt) temperature | 250 to 270 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Residual Moisture Content | 0.030 to 0.070 | % | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 60x60x2mm, 4 hr |
| 3. 60x60x2mm, 80°C MT, 600 bar |
| 4. 150x105x3mm, 4 hr |
| 5. 150x105x3mm, 80°C MT, 500 bar |
| 6. 0.079 in/min |
| 7. 2 mm/min |
| 8. 10°C/min |
| 9. Procedure A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |