| About |
|---|
| Durethan® BC700HTS 900116 DUSXBL (Dry) PA 6-Copolymer, non-reinforced, blow molding, heat-aging stabilized, improved impact strength, improved heat-aging stability. For the use in tank systems and pressure vessels please notice safety-related technical information within the High Performance Materials TechCenter under www.durethan-tank-systems.lanxess.com .&&Durethan® BC700HTS 900116 DUSXBL PA 6-Copolymer, non-reinforced, blow molding, heat-aging stabilized, improved impact strength, improved heat-aging stability. For the use in tank systems and pressure vessels please notice safety-related technical information within the High Performance Materials TechCenter under www.durethan-tank-systems.lanxess.com .&&Durethan® BC700HTS 900116 DUSXBL PA 6-Copolymer, non-reinforced, blow molding, heat-aging stabilized, improved impact strength, improved heat-aging stability. For the use in tank systems and pressure vessels please notice safety-related technical information within the High Performance Materials TechCenter under www.us.durethan-tank-systems.lanxess.com .&& |
| Product Description | |
|---|---|
| Supplier | LANXESS |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good heat aging resistance,High impact resistance,Copolymer,Heat Stabilized |
| Availabilitys | Africa & Middle East ,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03 | g/cm³ | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 8.1 | % | |
| Equilibrium, 23 ℃, 50% RH | 1.9 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 75 | kJ/m² | |
| 23℃ | 110 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 | ||
| Impact strength of cantilever beam notch | |||
| -30℃ | 70 | kJ/m² | |
| 23℃ | 90 | kJ/m² | |
| Notched impact strength of cantilever beam | |||
| Multi axial instrumented impact energy | |||
| -30 ℃, total impact penetration energy | 50.0 | J | |
| 23 ℃, total impact penetration energy | 50.0 | J | |
| Multi axial instrumented peak impact force | |||
| -30℃ | 4100 | N | |
| 23℃ | 3300 | N |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 53.0 | ℃ | |
| 1.8 MPa, unannealed | 48.0 | ℃ | |
| Melting temperature | 212 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD：23~55℃ | 2.0E-4 | 1/℃ | |
| TD：23~55℃ | 2.0E-4 | 1/℃ |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Shortname | ISO 1874-PA 6/66-HI, BHS, 14-010 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 23 ℃ | 65 | ||
| Tensile modulus | |||
| tensile strength | |||
| Yield, 23 ℃ | 28.0 | MPa | |
| Tensile strain | |||
| Yield, 23 ℃ | 6.5 | % | |
| Bending modulus | |||
| 23℃ | 980 | MPa | |
| bending strength | |||
| 23℃ | 35.0 | MPa | |
| 3.50% strain, 23 ℃ | 30.0 | MPa | |
| Bending strain | 6.1 | % |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying Temperature – Dry Air Dryer | 80 | °C | |
| Drying Time – Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (melt) temperature | 230 to 280 | °C | |
| Mold temperature | 60 to 90 | °C | |
| Residual Moisture Content | 0.0 to 0.060 | % | Karl Fisher |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. 2 mm/min |
| 4. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |