| About |
|---|
| Durethan® BG30XH3.0LT 904040 (Dry) PA 6, 30 % glass fibers/glass spheres, injection molding, heat-aging stabilized, low tendency to warp, NIR-laser transparent coloring (black)&&Durethan® BG30XH3.0LT 904040 PA 6, 30 % glass fibers/glass spheres, injection molding, heat-aging stabilized, low tendency to warp, NIR-laser transparent coloring (black)&&Durethan® BG30XH3.0LT 904040 PA 6, 30 % glass fibers/glass spheres, injection molding, heat-aging stabilized, low tendency to warp, NIR-laser transparent coloring (black)&& |
| Product Description | |
|---|---|
| Supplier | LANXESS |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Low warping,Heat Stabilized |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | |
| Apparent density | 0.70 | g/cm³ | |
| Shrinkage rate | |||
| TD：120℃，2.0 mm | 0.30 | % | |
| TD：280℃，2.0 mm | 0.80 | % | |
| MD：120℃，2.0 mm | 0.20 | % | |
| MD：280℃，2.0 mm | 0.50 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 7.0 | % | |
| Equilibrium, 23 ℃, 50% RH | 2.2 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -40℃ | < 10 | kJ/m² | |
| 23℃ | < 10 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 40 | kJ/m² | |
| 23℃ | 45 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| -30℃ | < 10 | kJ/m² | |
| Notched impact strength of cantilever beam | |||
| -30℃ | 30 | kJ/m² | |
| 23℃ | 35 | kJ/m² | |
| Multi axial instrumented impact energy | |||
| -30 ℃, total impact penetration energy | 1.70 | J | |
| 23 ℃, total impact penetration energy | 2.00 | J | |
| Multi axial instrumented peak impact force | |||
| -30℃ | 690 | N | |
| 23℃ | 700 | N |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 210 | ℃ | |
| 1.8 MPa, unannealed | 190 | ℃ | |
| Vicat Softening Temp | > 200 | ℃ | |
| Melting temperature | 222 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD：23~55℃ | 3.0E-5 | 1/℃ | |
| TD：23~55℃ | 9.0E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+14 | ohms | |
| Volume resistivity | |||
| 23℃ | 1.0E+15 | ohms·cm | |
| Relative permittivity | |||
| 23℃，100 Hz | 4.50 | ||
| 23℃，1 MHz | 4.00 | ||
| Dissipation factor | |||
| 23℃，100 Hz | 0.027 | ||
| 23℃，1 MHz | 0.022 | ||
| Compared to the leakage tracing index | |||
| Solution A | 375 | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| US FMVSS302 | passed | ||
| Flame retardant level | |||
| 1.50 mm | HB | ||
| Glowing wire flammability index | |||
| 2.0 mm | 650 | ℃ |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Shortname | ISO 1874-PA 6,GHR,14-060, (GB+GF)30 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | 185 | MPa | |
| Tensile modulus | |||
| 23℃ | 6210 | MPa | |
| 23℃ | 6400 | MPa | |
| tensile strength | |||
| Fracture, 23 ℃ | 121 | MPa | |
| Fracture, 23 ℃ | 120 | MPa | |
| Tensile strain | |||
| Fracture, 23 ℃ | 4.0 | % | |
| Tensile creep modulus | |||
| 1 hr | — | MPa | |
| 1000 hr | — | MPa | |
| Bending modulus | |||
| 23℃ | 5800 | MPa | |
| bending strength | |||
| 23℃ | 195 | MPa | |
| 23℃ | 185 | MPa | |
| 3.50% strain, 23 ℃ | 170 | MPa | |
| Bending strain | 5.0 | % |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying Temperature – Dry Air Dryer | 80 | °C | |
| Drying Time – Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (melt) temperature | 270 to 290 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 60x60x2mm, 4 hr |
| 3. 60x60x2mm, 80°C MT, 600 bar |
| 4. 0.079 in/min |
| 5. 2 mm/min |
| 6. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |