| About |
|---|
| 注塑成型，30%玻纤增强，弹性体改性，在双轴冲击负荷下提高无缺口冲击强度和能量吸收，热稳定 |
| Product Description | |
|---|---|
| Supplier | LANXESS |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1360 | ISO 1183 | |
| Shrinkage rate | |||
| MD：150x105x3，280℃ / MT 80℃， 500 bar | 0.16 | % | ISO 2577 |
| Normal, 150x105x3280 ℃/MT 80 ℃, 500 bar | 0.72 | % | ISO 2577 |
| Post contraction | |||
| Parallel, 150x105x3; 120 ℃; 4 hours | 0.04 | % | ISO 2577 |
| 正常,150x105x3; 120 °C; 4 h | 0.15 | % | ISO 2577 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 1 mm/min | 9000 | MPa | ISO 527-1 |
| Fracture stress | |||
| 5 mm/min | 160 | MPa | ISO 527-1 |
| Fracture strain | |||
| 5 mm/min | 4.0 | % | ISO 527-1 |
| Tensile creep modulus | |||
| 1 h | 4200 | MPa | ISO 899-1 |
| 1 000h | 3300 | MPa | ISO 899-1 |
| Bending modulus | |||
| 2 mm/mim | 8000 | MPa | ISO 178 |
| bending strength | |||
| 2 mm/min | 250 | MPa | ISO 178 |
| Bending strain | |||
| 2 mm/min | 5.0 | % | ISO 178 |
| bending strength | |||
| 3.50% strain, 2 mm/min | 230 | MPa | ISO 178 |
| Puncture energy | |||
| 23 ℃ | 10 | J | ISO 6603-2 |
| -30 ℃ | 7 | J | ISO 6603-2 |
| ball indentation hardness | 190 | N/mm² | ISO 2039-1 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| 10℃ / min | 213 | ℃ | ISO 11357-1 |
| Hot deformation temperature | |||
| 1.8 MPa | 200 | ℃ | ISO 75-1/2 |
| 0.45 MPa | 210 | ℃ | ISO 75-1/2 |
| 8.0 MPa | 90 | ℃ | ISO 75-1/2 |
| Vicat Softening Temp | |||
| B120 | >200 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| Parallel, 23-55 ℃ | 0.2 | 10 -4 /K | ISO 11359-1,-2 |
| Horizontal: 23~55 ℃ | 0.9 | 10 -4 /K | ISO 11359-1,-2 |
| Flame retardant level | |||
| 1.60 mm | HB | 等级 | UL 94 |
| HB | 等级 | UL 94 | |
| Extreme oxygen index | 22 | % | ISO 4589-2 |
| Glowing wire flammability index | |||
| 2.0 mm | 650 | ℃ | IEC 60695-2-12 |
| Thermal conductivity | |||
| 23 ℃ | 0.3 | W/(m·K) | SO 8302 |
| specific heat | |||
| 23 ℃ | 1.1 | kJ/(kg·K) | |
| Temperature index (tensile strength) | |||
| 5000 h | 175 | ℃ | IEC 60216-1 |
| 20000 h | 145 | ℃ | IEC 60216-1 |
| tensile strength | |||
| Half time interval | 13.5 | ℃ | IEC 60216-1 |
| Temperature index (tensile impact strength) | |||
| 5000 h | 140 | ℃ | IEC 60216-1 |
| 20000 h | 120 | ℃ | IEC 60216-1 |
| Half time interval (tensile impact strength) | 12.0 | ℃ | IEC 60216-1 |
| Temperature index (dielectric strength) | |||
| 5000 h | 180 | ℃ | IEC 60216-1 |
| 20000 h | 150 | ℃ | IEC 60216-1 |
| Dielectric strength | |||
| Half time interval | 40 | kV/mm | IEC 60216-1 |
| Relative temperature index | |||
| tensile strength | 130 | ℃ | UL 746B |
| Tensile impact strength | 105 | ℃ | UL 746B |
| Dielectric strength | 130 | ℃ | UL 746B |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative permittivity | |||
| 100 Hz | 4.0 | IEC 60250 | |
| 1 MHz | 4.0 | IEC 60250 | |
| Volume resistivity | 1E+15 | ohms·cm | IEC 60093 |
| Surface resistivity | 1.0E+14 | ohms | IEC 60093 |
| Medium strength | |||
| 1 mm | 40 | kV/mm | IEC 60243-1 |
| Other performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Water absorption rate | |||
| Static, 23 ℃ | 7 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 2.0 | % | ISO 62 |
| Fiberglass content | 30 | % | ISO 3451-1 |
| bulk density | 700 | kg/m³ | ISO 60 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 18 | kJ/m² | ISO 179-1eA |
| -30℃ | 10 | kJ/m² | ISO 179-1eA |
| Charpy impact strength | |||
| 23℃ | 95 | kJ/m² | ISO 179-1eU |
| -30℃ | 80 | kJ/m² | ISO 179-1eU |
| Impact strength of cantilever beam notch | |||
| 23℃ | 16 | kJ/m² | ISO 180-1A |
| -30℃ | 10 | kJ/m² | ISO 180-1A |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Melt temperature | 280 | °C | ISO 294 |
| Mold temperature | 80 | °C | ISO 294 |
| Injection speed | 200 | mm/s | ISO 294 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |