Durethan® BKV 30

About
注塑成型，30%玻纤增强，热稳定

Product Description
Supplier	LANXESS
Generic	PA6
Material Status	Commercial: Active
Availabilitys	Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.36	g/cm³	ISO 1183
Melt Volume Rate
260℃，5 kg	14	cm³/10min	ISO 1133
Shrinkage rate
MD：150x105x3，280℃ / MT 80℃， 500 bar	0.18	%	ISO 2577
Normal, 150x105x3280 ℃/MT 80 ℃, 500 bar	0.85	%	ISO 2577
Post contraction
Parallel, 150x105x3; 120 ℃; 4 hours	0.04	%	ISO 2577
正常,150x105x3; 120 °C; 4 h	0.11	%	ISO 2577

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
1 mm/min	9500	MPa	ISO 527-1
Fracture stress
5 mm/min	170	MPa	ISO 527-1
Fracture strain
5 mm/min	3.0	%	ISO 527-1
Tensile creep modulus
1 h	5100	MPa	ISO 899-1
1 000h	4100	MPa	ISO 899-1
Bending modulus
2 mm/mim	8300	MPa	ISO 178
bending strength
2 mm/min	270	MPa	ISO 178
Bending strain
2 mm/min	4.0	%	ISO 178
bending strength
3.50% strain, 2 mm/min	140	MPa	ISO 178
Puncture energy
23 ℃	6	J	ISO 6603-2
-30 ℃	4	J	ISO 6603-2
ball indentation hardness	210	N/mm²	ISO 2039-1

THERMAL	Nominal value	Unit	Test method
Melting temperature
10℃ / min	222	℃	ISO 11357-1
Hot deformation temperature
1.8 MPa	200	℃	ISO 75-1/2
0.45 MPa	215	℃	ISO 75-1/2
8.0 MPa	110	℃	ISO 75-1/2
Vicat Softening Temp
B120	>200	℃	ISO 306
Linear coefficient of thermal expansion
Parallel, 23-55 ℃	0.2	10 -4 /K	ISO 11359-1,-2
Horizontal: 23~55 ℃	0.8	10 -4 /K	ISO 11359-1,-2
Flame retardant level
1.60 mm	HB	等级	UL 94
	HB	等级	UL 94
Extreme oxygen index	22	%	ISO 4589-2
Glowing wire flammability index
2.0 mm	600	℃	IEC 60695-2-12
Thermal conductivity
23 ℃	0.3	W/(m·K)	SO 8302
specific heat
23 ℃	1.0	kJ/(kg·K)
Temperature index (tensile strength)
5000 h	170	℃	IEC 60216-1
20000 h	145	℃	IEC 60216-1
tensile strength
Half time interval	8.3	℃	IEC 60216-1
Temperature index (tensile impact strength)
5000 h	125	℃	IEC 60216-1
20000 h	105	℃	IEC 60216-1
Half time interval (tensile impact strength)	9.3	℃	IEC 60216-1
Temperature index (dielectric strength)
5000 h	165	℃	IEC 60216-1
20000 h	145	℃	IEC 60216-1
Dielectric strength
Half time interval	40	kV/mm	IEC 60216-1
Relative temperature index
tensile strength	130	℃	UL 746B
Tensile impact strength	95	℃	UL 746B
Dielectric strength	120	℃	UL 746B
Burning rate	通过	mm/min	ISO 3795

Electrical performance	Nominal value	Unit	Test method
Relative permittivity
100 Hz	4.2		IEC 60250
1 MHz	3.8		IEC 60250
Loss factor
100 Hz	100	10 -4	IEC 60250
1 MHz	170	10 -4	IEC 60250
Volume resistivity	1E+15	ohms·cm	IEC 60093
Surface resistivity	1.0E+14	ohms	IEC 60093
Medium strength
1 mm	40	kV/mm	IEC 60243-1
Compared to the leakage tracing index
Solution A	425		IEC 60112
Solution B	300M		IEC 60112
Electrolytic corrosion	A/B 3		IEC 60426

Other performance	Nominal value	Unit	Test method
Water absorption rate
Static, 23 ℃	7	%	ISO 62
Equilibrium, 23 ℃, 50% RH	2.1	%	ISO 62
Fiberglass content	30	%	ISO 3451-1
bulk density	700	kg/m³	ISO 60

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	10	kJ/m²	ISO 179-1eA
-30℃	<10	kJ/m²	ISO 179-1eA
Charpy impact strength
23℃	80	kJ/m²	ISO 179-1eU
-30℃	70	kJ/m²	ISO 179-1eU
Impact strength of cantilever beam notch
-30℃	<10	kJ/m²	ISO 180-1A

Process Conditions
injection molding	Nominal value	Unit	Test method
Melt temperature	280	°C	ISO 294
Mold temperature	80	°C	ISO 294
Injection speed	200	mm/s	ISO 294

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.