| About |
|---|
| Durethan® BKV50H2.0EF 900116 (Dry) PA 6, 50 % glass fibers, injection molding, improved flowability, heat-aging stabilized&&Durethan® BKV50H2.0EF 900116 PA 6, 50 % glass fibers, injection molding, improved flowability, heat-aging stabilized&&Durethan® BKV50H2.0EF 900116 PA 6, 50 % glass fibers, injection molding, improved flowability, heat-aging stabilized&& |
| Product Description | |
|---|---|
| Supplier | LANXESS |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good heat aging resistance,Good liquidity,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.57 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：2.0 mm | 0.19 | % | ISO 294-4 |
| TD：2.0 mm | 0.60 | % | ISO 294-4 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 220 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, annealed | 210 | ℃ | ISO 75-2/Af |
| Melting temperature | 222 | ℃ | ISO 11357-3 |
| Vicat Softening Temp | |||
| Linear coefficient of thermal expansion | |||
| MD | 1.2E-5 | 1/℃ | ISO 11359-2 |
| TD | 9.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 7.0E+14 | Ω.cm | IEC 60093 |
| Insulation strength | |||
| 1.00mm | 35 | KV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 23℃ | 4.70 | 100 Hz | IEC 60250 |
| 23℃ | 4.20 | 1 MHz | IEC 60250 |
| Dissipation factor | |||
| 23℃ | 0.014 | 100 Hz | IEC 60250 |
| 23℃ | 0.017 | 1 MHz | IEC 60250 |
| Compared to the leakage tracing index | 400 | V | IEC 60112 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | 232 | MPa | ISO 2039-1 |
| tensile strength | |||
| 23℃ | 215 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.70 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃ | 16200 | MPa | ISO 527-2 |
| bending strength | |||
| 23℃ | 340 | MPa | ISO 178 |
| Bending modulus | |||
| 23℃ | 15000 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 17 | kJ/m² | ISO 180-1A |
| -30℃ | 15 | kJ/m² | ISO 180-1A |
| Charpy Unnotch Impact strength | |||
| 23℃ | 100 | kJ/m² | ISO 179/1eU |
| -30℃ | 95 | kJ/m² | ISO 179/1eU |
| Notched impact strength of cantilever beam | |||
| 23℃ | 85 | kJ/m² | ISO 180/1U |
| -30℃ | 85 | kJ/m² | ISO 180/1U |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2-6 | Hr | |
| Injection temperature | |||
| Mold temperature | 80-120 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 60x60x2mm, 4 hr |
| 3. 60x60x2mm, 80°C MT, 600 bar |
| 4. 0.079 in/min |
| 5. 2 mm/min |
| 6. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |