| About |
|---|
| Durethan® BKV130GIT 900116 DUS008 (Dry) PA 6, 30 % glass fibers, injection molding, improved impact strength, GIT/WIT&&Durethan® BKV130GIT 900116 DUS008 PA 6, 30 % glass fibers, injection molding, improved impact strength, GIT/WIT&&Durethan® BKV130GIT 900116 DUS008 PA 6, 30 % glass fibers, injection molding, improved impact strength, GIT/WIT&& |
| Product Description | |
|---|---|
| Supplier | LANXESS |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | High impact resistance |
| Availabilitys | North America,Latin America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | |
| Shrinkage rate | |||
| TD：120℃，2.0 mm | 0.15 | % | |
| TD：280℃，2.0 mm | 0.50 | % | |
| MD：120℃，2.0 mm | 0.060 | % | |
| MD：280℃，2.0 mm | 0.20 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 9000 | MPa | |
| tensile strength | |||
| Fracture, 23 ℃ | 160 | MPa | |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.4 | % | |
| Bending modulus | |||
| 23℃ | 8500 | MPa | |
| bending strength | |||
| 23℃ | 256 | MPa | |
| 3.50% strain, 23 ℃ | 230 | MPa | |
| Bending strain | 4.1 | % |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 10 | kJ/m² | |
| 23℃ | 15 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 65 | kJ/m² | |
| 23℃ | 85 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| -30℃ | 10 | kJ/m² | |
| 23℃ | 15 | kJ/m² | |
| Notched impact strength of cantilever beam | |||
| -30℃ | 60 | kJ/m² | |
| 23℃ | 75 | kJ/m² | |
| Multi axial instrumented impact energy | |||
| -30 ℃, total impact penetration energy | 2.50 | J | |
| 23 ℃, total impact penetration energy | 3.80 | J | |
| Multi axial instrumented peak impact force | |||
| -30℃ | 770 | N | |
| 23℃ | 935 | N |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 210 | ℃ | |
| 1.8 MPa, unannealed | 195 | ℃ | |
| Vicat Softening Temp | 200 | ℃ | |
| Melting temperature | 220 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD：23~55℃ | 2.0E-5 | 1/℃ | |
| TD：23~55℃ | 9.0E-5 | 1/℃ |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Shortname | ISO 1874-PA 6-HI, GR, 14-090, GF30 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying Temperature – Dry Air Dryer | 80 | °C | |
| Drying Time – Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (melt) temperature | 260 to 290 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 60x60x2mm, 4 hr |
| 3. 60x60x2mm, 80°C MT, 600 bar |
| 4. 0.079 in/min |
| 5. 2 mm/min |
| 6. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |