| About |
|---|
| Durethan® DPAKV30HREF 901510 (Dry) PA 66, 30 % glass fibers, injection molding, improved flowability, heat-aging stabilized, hydrolysis stabilized&&Durethan® DPAKV30HREF 901510 PA 66, 30 % glass fibers, injection molding, improved flowability, heat-aging stabilized, hydrolysis stabilized&&Durethan® DPAKV30HREF 901510 PA 66, 30 % glass fibers, injection molding, improved flowability, heat-aging stabilized, hydrolysis stabilized&& |
| Product Description | |
|---|---|
| Supplier | LANXESS |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good heat aging resistance,Hydrolysis stability,Good liquidity,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.32 | g/cm³ | ISO 1183 |
| Apparent density | 0.70 | g/cm³ | ISO 60 |
| Shrinkage rate | ISO 294-4 | ||
| TD：290℃，2.0 mm | 0.82 | % | ISO 294-4 |
| TD：120℃，2.0 mm，2 hrs | 0.040 | % | ISO 294-4 |
| MD：290℃，2.0 mm | 0.37 | % | ISO 294-4 |
| MD：120℃，2.0 mm，2 hrs | 0.060 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 8200 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 150 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.6 | % | ISO 527-2/5 |
| Bending modulus | |||
| 23℃ | 8100 | MPa | ISO 178-A |
| bending strength | |||
| 3.50% strain | 225 | MPa | ISO 178-A |
| 23℃ | 240 | MPa | ISO 178 |
| Bending strain | 4.0 | % |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Membrane puncture strength | ISO 6603-2 | ||
| — | 2.50 | J | ISO 6603-2 |
| — | 2.70 | J | ISO 6603-2 |
| Membrane puncture force | ISO 6603-2 | ||
| — | 756 | N | ISO 6603-2 |
| — | 774 | N | ISO 6603-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | < 10 | kJ/m² | ISO 179/1eA |
| 23℃ | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 70 | kJ/m² | ISO 179/1eU |
| 23℃ | 80 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | < 10 | kJ/m² | ISO 180-1A |
| 23℃ | 10 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -30℃ | 65 | kJ/m² | ISO 180/1U |
| 23℃ | 70 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 240 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 250 | ℃ | ISO 75-2/B |
| Melting temperature | 263 | ℃ | ISO 11357-3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | passed | ISO 3795 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Shortname | PA 66, GHRW, 14-080, GF30 | ISO 1874 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying Temperature – Dry Air Dryer | 80 | °C | |
| Drying Time – Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Residual Moisture Content | 0.030 to 0.12 | % | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 60x60x2mm, 4 hr |
| 3. 60x60x2mm, 80°C MT, 600 bar |
| 4. 0.079 in/min |
| 5. 2 mm/min |
| 6. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |