| About |
|---|
| Product Description | |
|---|---|
| Supplier | LANXESS |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good heat aging resistance,Heat Stabilized,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | ISO 1183 |
| Apparent density | 0.70 | g/cm³ | ISO 60 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 7.0 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 2.1 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 9400 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 145 | MPa | ISO 527-1-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.0 | % | ISO 527-2/1 |
| Bending modulus | |||
| 23℃ | 8900 | MPa | ISO 178-A |
| bending strength | |||
| 23℃ | 35 | MPa | ISO 178-A |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | <=1.0 | J/cm² | ISO 179/1eA |
| 23℃ | <=1.0 | J/cm² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 5.5 | kJ/m² | ISO 179/1eU |
| 23℃ | 6.5 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| 23℃ | <=10 | kJ/m² | ISO 180-1A |
| -30℃ | <=10 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -30℃ | 50 | kJ/m² | ISO 180/1U |
| 23℃ | 55 | kJ/m² | ISO 180/1U |
| Ball hardness | 210 | MPa | ISO 2039-1 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 197 | ℃ | ISO 75-1/2 |
| 0.46 MPa, unannealed | 215 | ℃ | ISO 75-1/2 |
| melting point | 220 | ℃ | ISO 11357-3/-1 |
| Processing | Nominal value | Unit | Test method |
|---|---|---|---|
| Melt Temperature | 270 – 290 | ℃ | ISO 294-4 |
| Mold temperature | 80.0 – 120 | °C | ISO 294-4 |
| drying temperature | 80.0 | °C | – |
| drying time | 2-6 | hr | – |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |