| Durethan® T40 000000 (Dry) PA 6I, non-reinforced, injection molding, extrusion&&Durethan® T40 000000 PA 6I, non-reinforced, injection molding, extrusion&&Durethan® T40 000000 PA 6I, non-reinforced, injection molding, extrusion&& |
| Product Description | |
|---|---|
| Supplier | LANXESS |
| Generic | PA6I |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | |
| Shrinkage rate | |||
| TD：100℃，3.0 mm | 0.090 | % | |
| TD：270℃，3.0 mm | 0.49 | % | |
| MD：100℃，3.0 mm | 0.13 | % | |
| MD：270℃，3.0 mm | 0.53 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 6.0 | % | |
| Equilibrium, 23 ℃, 50% RH | 2.0 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 3000 | MPa | |
| tensile strength | |||
| Yield, 23 ℃ | 110 | MPa | |
| Tensile strain | |||
| Yield, 23 ℃ | 6.0 | % | |
| Bending modulus | |||
| 23℃ | 3000 | MPa | |
| bending strength | |||
| 23℃ | 150 | MPa | |
| 3.50% strain, 23 ℃ | 105 | MPa | |
| Bending strain | 7.0 | % |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -40℃ | < 10 | kJ/m² | |
| -30℃ | < 10 | kJ/m² | |
| 23℃ | < 10 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 | ||
| Impact strength of cantilever beam notch | |||
| -40℃ | < 10 | kJ/m² | |
| -30℃ | < 10 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 115 | ℃ | |
| 1.8 MPa, unannealed | 105 | ℃ | |
| Vicat Softening Temp | 125 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD：23~55℃ | 7.0E-5 | 1/℃ | |
| TD：23~55℃ | 8.0E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+15 | ohms | |
| Volume resistivity | |||
| 23℃ | 1.0E+15 | ohms·cm | |
| Dielectric strength | |||
| 23 ℃，1 mm | 25 | kV/mm | |
| Relative permittivity | |||
| 23℃，100 Hz | 4.30 | ||
| 23℃，1 MHz | 3.80 | ||
| Dissipation factor | |||
| 23℃，100 Hz | 0.040 | ||
| 23℃，1 MHz | 0.090 | ||
| Compared to the leakage tracing index | |||
| Solution A | 600 | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | V-2 | ||
| 1.50 mm | V-2 | ||
| Glowing wire flammability index | |||
| 2.0 mm | 960 | ℃ |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Shortname | ISO 1874-PA 6I, GT, 12-030 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying Temperature – Dry Air Dryer | 80 | °C | |
| Drying Time – Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (melt) temperature | 260 to 280 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 150x105x3mm, 4 hr |
| 3. 150x105x3mm, 80°C MT, 500 bar |
| 4. 0.039 in/min |
| 5. 0.079 in/min |
| 6. 2 mm/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |