| Medium flow rate and high impact grade. For injection molding. Main applications: automotive and electrical-electronic.&& |
| Product Description | |
|---|---|
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,Moderate liquidity,HB |
| Availabilitys | North America,Latin America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.15 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 12 | g/10min | ASTM D1238，ISO 1133 |
| Shrinkage rate | |||
| MD | 0.55 to 0.75 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.20 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2200 | MPa | ASTM D638 , ISO 527-2 |
| tensile strength | ASTM D638 , ISO 527-2 | ||
| yield | 53.0 | MPa | ASTM D638 , ISO 527-2 |
| fracture | 53.0 | MPa | ASTM D638 , ISO 527-2 |
| Tensile strain | ASTM D638 , ISO 527-2 | ||
| yield | 5.0 | % | ASTM D638 , ISO 527-2 |
| fracture | 130 | % | ASTM D638 , ISO 527-2 |
| Bending modulus | 2300 | MPa | ASTM D790 , ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃，3.2mm | 340 | J/m | ASTM D256 |
| 23℃，3.2mm | 600 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 127 | ℃ | ASTM D648，ISO 75-2/B |
| 1.8 MPa, unannealed, 3.2 mm | 109 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 109 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B120 | 135 | ℃ | ASTM D1525 2 , ISO 306/B120 2 |
| B50 | 133 | ℃ | ASTM D1525 3 , ISO 306/B50 3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 | °C | |
| Drying time | 4.0 | hr | |
| Barrel rear temperature | 250 | °C | |
| Barrel middle temperature | 260 | °C | |
| Barrel front temperature | 270 | °C | |
| Nozzle temperature | 260 | °C | |
| Processing (melt) temperature | 240 to 280 | °C | |
| Mold temperature | 70 to 100 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |