| About |
|---|
| Flame Retardant TPU Features: Excellent Chemical Resistance Low Temperature Properties Good Processability Applications: Wire & Cable Industrial Automotive&& |
| Product Description | |
|---|---|
| Generic | TPU |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Halogen free,Flame Characteristics,Solvent resistance,Low temperature toughness,low-temperature impact resistance,Low temperature strength,V-0 |
| Availabilitys | North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
| 1.60 mm | V-0 | UL 94 | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 85 | ASTM D2240 | |
| tensile strength | |||
| fracture | 14.5 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 500 | % | ASTM D638 |
| Bending modulus | 60.7 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 3.0 to 6.0 | hr | |
| Barrel rear temperature | 160 to 168 | °C | |
| Barrel middle temperature | 166 to 174 | °C | |
| Barrel front temperature | 168 to 174 | °C | |
| Nozzle temperature | 168 to 174 | °C | |
| Processing (melt) temperature | 168 to 174 | °C | |
| Mold temperature | 10 to 38 | °C | |
| Injection pressure | 68.9 to 138 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |