| About |
|---|
| ebalta AH 120/TL is a very thin liquid epoxy resin with high values of strength and dimensional stability. Due to its good impregnating and wetting properties it is suitable as laminating resin for high-strength components with fabrics of glass -or carbon fiber. ebalta AH 120/TL is suitable for laminating of thin as well as thick laminates with large surface up to a thickness of 20 mm. A post-curing should be executed, if possible before demoulding. Applications Laminating resin also for heavy fabrics/bonded fabrics Vehicle construction Aircraft construction Properties unfilled high heat resistance low viscosity high strength&& |
| Product Description | |
|---|---|
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,Low Viscosity,High Heat Resistance |
| Availabilitys | Africa & Middle East ,North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Charpy Unnotch Impact strength | 45 to 55 | kJ/m² | ISO 179 |
| Uncured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | |||
| 20℃ | 1.09 to 1.13 | g/cm³ | |
| viscosity | |||
| 25℃ | 0.70 to 0.90 | Pa·s | |
| Curing time | |||
| 20℃ | 18 to 24 | hr | |
| storage stability | |||
| 20 ℃ | 80 to 90 | min |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 84 to 88 | ISO 7619 | |
| Bending modulus | 3050 to 3550 | MPa | ISO 178 |
| bending strength | 115 to 135 | MPa | ISO 178 |
| compressive strength | 97.0 to 117 | MPa | ISO 604 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 95.0 to 101 | ℃ | ISO 75-2/B |
| Thermosetting components | |||
| resin | 按重量计算的混合比: 100 | ||
| Hardening method | 按重量计算的混合比: 25 | ||
| Post curing time | |||
| 60℃ | 6.0 to 8.0 | hr | |
| 90℃ | 3.0 to 5.0 | hr |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 200 g |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |